SABIC® PP 90910
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | Saudi Basic Industries Corporation (SABIC) |
| Trademark: | SABIC® PP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 0clkUD_SABIC-PP-90910.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
SABIC® PP 90910 is a reactor-elastomer-modified material which offers a good cold impact resistance in combination with high flow. It is a highly attractive alternative to non-filled compounds and is typically used for painted car bumpers and exterior trim. SABIC® PP 90910 is a designated automotive grade. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.900 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 22 | g/10 min | ASTM D1238, ISO 1133 |
| Molding Shrinkage | Internal Method | ||
| Flow : 24 hr | 1.6 | % | |
| 24 hr | 1.6 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore D, Injection Molded) | 50 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| 1% Secant : Injection Molded 1 | 950 | MPa | ASTM D638 |
| Injection Molded | 850 | MPa | ISO 527-2/1A/1 |
| Tensile Strength | |||
| Yield, Injection Molded 2 | 18.0 | MPa | ASTM D638 |
| Yield, Injection Molded | 18.0 | MPa | ISO 527-2/1A/50 |
| Tensile Elongation | |||
| Yield, Injection Molded 3 | 8.0 | % | ASTM D638 |
| Yield, Injection Molded | 8.0 | % | ISO 527-2/1A/50 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| 0°C, Injection Molded | No Break | ||
| 23°C, Injection Molded | No Break | ||
| Notched Izod Impact | |||
| -20°C, Injection Molded | 200 | J/m | ASTM D256A |
| 0°C, Injection Molded | No Break | ASTM D256A, ISO 180/1A | |
| 23°C, Injection Molded | No Break | ASTM D256A, ISO 180/1A | |
| -20°C, Injection Molded | 15 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | |||
| -- | 125 | °C | ASTM D1525, ISO 306/A120 4 4 |
| -- | 49.0 | °C | ASTM D1525, ISO 306/B120 5 5 |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | 50 mm/min |
| 3 . | 50 mm/min |
| 4 . | Rate B (120°C/h), Loading 1 (10 N) |
| 5 . | Rate B (120°C/h), Loading 2 (50 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Next Nylon 66 Prime Series PST-01NC | Next Polymers Ltd. | Nylon 66 | Next Nylon 66 Prime Series |
| Anjacom® R350-H/GF35 | Almaak International GmbH | Nylon 66 | Anjacom® |
| Duratuf™ 830U2/X | Technical Polymers, LLC | Acetal (POM) Copolymer | Duratuf™ |
| HAIPLEN H10 G4 BA | Taro Plast S.p.A. | PP Homopolymer | HAIPLEN |
| POLYCOMPO PE SP1520 | POLYCOMPO Co.,Ltd. | LLDPE | POLYCOMPO PE |