| 15% Glass Reinforced, Heat Stabilized, Polyamide 6 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Forms |
|
| Processing Method |
|
| Part Marking Code (ISO 11469) |
|
| Resin ID (ISO 1043) |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.25 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | |||
| Across Flow | 0.80 | -- | % | |
| Flow | 0.30 | -- | % | |
| Water Absorption | ISO 62 | |||
| 23°C, 24 hr, 2.00 mm | 7.6 | -- | % | |
| Equilibrium, 23°C, 2.00 mm, 50% RH | 2.5 | -- | % | |
| Viscosity Number | 150 | -- | cm³/g | ISO 307 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 6500 | 4000 | MPa | ISO 527-2 |
| Tensile Stress (Break) | 130 | 80.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 2.3 | 10 | % | ISO 527-2 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -30°C | 5.0 | 7.0 | kJ/m² | |
| 23°C | 6.0 | 7.0 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
| -30°C | 40 | 40 | kJ/m² | |
| 23°C | 40 | 70 | kJ/m² |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, Unannealed | 220 | -- | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 204 | -- | °C | ISO 75-2/A |
| Vicat Softening Temperature | 215 | -- | °C | ISO 306/B50 |
| Melting Temperature 1 | 221 | -- | °C | ISO 11357-3 |
| CLTE | ISO 11359-2 | |||
| Flow | 3.5E-5 | -- | cm/cm/°C | |
| Transverse | 1.1E-4 | -- | cm/cm/°C |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Electric Strength | 22 | -- | kV/mm | IEC 60243-1 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Burning Rate (1.00 mm) | 25 | -- | mm/min | ISO 3795 |
| Flammability Classification (1.50 mm) | HB | -- | IEC 60695-11-10, -20 | |
| Oxygen Index | 21 | -- | % | ISO 4589-2 |
| Fill Analysis | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Thermal Conductivity of Melt | 0.20 | -- | W/m/K |
| Additional Information | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Emission of Organic Compounds | 8.50 | -- | µgC/g | VDA 277 |
| Odor | 4 | -- | VDA 270 |
| Note Message | |
|---|---|
| 1 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| ELASTOSIL® R 750/40 | Wacker Chemie AG | Silicone | ELASTOSIL® R |
| Generic PVC+PUR | Generic | PVC+PUR | Generic |
| EnviroPro 5020GF35 | West Michigan Compounding | PP, Unspecified | EnviroPro |
| Hostacom ERC 204N G71322 | LyondellBasell Industries | PP Copolymer | Hostacom |
| MAXAMID™ RC6G30HSL-BK09 | Pier One Polymers, Inc. | Nylon 6 | MAXAMID™ |