Versaflex™ 9570-9
| Category: | TPE , Thermoplastic Elastomer |
| Manufacturer: | PolyOne Corporation |
| Trademark: | Versaflex™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 0aMgwd_Versaflex-9570-9.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
Versaflex™9570-9 has strong fluidity and good surface aesthetic effect, which is suitable for various applications.
|
| General Information | |
|---|---|
| Features |
|
| Agency Ratings |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.988 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) | ASTM D1238 | ||
| 190°C/2.16 kg | 7.7 | g/10 min | ASTM D1238 |
| 200°C/5.0 kg | 57 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 0.90 - 1.6 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore A, 10 sec) | 69 | ASTM D2240 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress 1 | ASTM D412 | ||
| 100% strain, 23°C 2 | 2.14 | MPa | ASTM D412 |
| 300% strain, 23°C 3 | 3.45 | MPa | ASTM D412 |
| Tensile Strength (Break, 23°C) | 5.52 | MPa | ASTM D412 |
| Tensile Elongation (Break, 23°C) | 600 | % | ASTM D412 |
| Compression Set (23°C, 22 hr) | 26 | % | ASTM D395B |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.50 mm) | HB | UL 94 |
| Fill Analysis | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Apparent Viscosity | ASTM D3835 | ||
| 200°C, 1340 sec^-1 | 33.0 | Pa·s | ASTM D3835 |
| 200°C, 11200 sec^-1 | 7.40 | Pa·s | ASTM D3835 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Suggested Max Regrind | 20 | % | |
| Rear Temperature | 149 - 188 | °C | |
| Middle Temperature | 160 - 199 | °C | |
| Front Temperature | 171 - 210 | °C | |
| Nozzle Temperature | 171 - 210 | °C | |
| Mold Temperature | 15.6 - 26.7 | °C | |
| Back Pressure | 0.00 - 0.689 | MPa | |
| Screw Speed | 50 - 100 | rpm |
| Injection instructions |
|---|
| 在使用此产品之前或之后，均须用熔体流动速率较低 (0.5 - 2.5 MFR) 的聚乙烯 (PE) 或聚丙烯 (PP) 彻底进行置换。Versaflex™ 9570-9 可利用高达 20% 的回收料同时其性能所受影响却极小，但该回收料必须是未受到污染的。为了最大限度地减小模塑期间其性能所受的影响，熔体温度应维持得尽可能低。回收料的有效性应由用户最终确定。Versaflex™ 9570-9 具有良好的熔体稳定性。如果机器闲置十五 (15) 分钟或以上，则应将机筒排空。不需要干燥注射速度：1 - 5 英寸/秒第一阶段 - 提升压力：300 - 700 psi第二阶段 - 保持压力：30% 的升压保持时间（厚部件）：4 - 10 秒保持时间（薄部件）：1 - 3 秒 |
| Note Message | |
|---|---|
| 1 . | 2 hours |
| 2 . | Mouth die c |
| 3 . | C mould |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Shin-Etsu Elastomer SV-17500U | Shin-Etsu Silicones of America | Silicone Rubber, HTV | Shin-Etsu Elastomer |
| TRIBOCOMP® PA66 CF30 TS0 | EPIC Polymers | Nylon 66 | TRIBOCOMP® |
| NEOFLON™ EC-6519 | DAIKIN AMERICA, INC. | ETFE | NEOFLON™ |
| Hostaform® C 13031 LS | Celanese Corporation | Acetal (POM) Copolymer | Hostaform® |
| RONFALIN® ABS 1413 GB 20 | A. Schulman Europe | ABS | RONFALIN® |