Generic LMDPE
| Category: | LMDPE , Linear Medium Density Polyethylene |
| Manufacturer: | Generic |
| Trademark: | Generic |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 0aI4TC_Generic-LMDPE.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
This data represents typical values that have been calculated from all products classified as: Generic LMDPE This information is provided for comparative purposes only. |
| General Information |
|---|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 0.934 to 0.938 | g/cm³ | ASTM D792 |
| 23°C | 0.934 to 0.940 | g/cm³ | ISO 1183 |
| -- | 0.914 to 0.959 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) | |||
| 190°C/2.16 kg | 3.9 to 6.1 | g/10 min | ASTM D1238 |
| 190°C/2.16 kg | 3.3 to 6.1 | g/10 min | ISO 1133 |
| Environmental Stress-Cracking Resistance (23°C) | 27.9 to 1000 | hr | ASTM D1693 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness | |||
| 23°C | 60 to 65 | ASTM D2240 | |
| 23°C | 55 to 57 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 646 to 758 | MPa | ISO 527-2 |
| Tensile Strength | |||
| Yield, 23°C | 17.9 to 20.0 | MPa | ASTM D638 |
| Yield, 23°C | 18.0 to 22.0 | MPa | ISO 527-2 |
| Tensile Strain | |||
| Yield, 23°C | 11 to 12 | % | ISO 527-2 |
| Break, 23°C | 380 to 1000 | % | ASTM D638 |
| Break, 23°C | 88 to 1000 | % | ISO 527-2 |
| Flexural Modulus | |||
| 23°C | 556 to 862 | MPa | ASTM D790 |
| 23°C | 698 to 803 | MPa | ISO 178 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 20 to 26 | µm |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed | 63.9 to 71.5 | °C | ASTM D648 |
| 0.45 MPa, Unannealed | 64.8 to 68.2 | °C | ISO 75-2/B |
| Brittleness Temperature | -70.2 to -70.0 | °C | ASTM D746 |
| Vicat Softening Temperature | 113 to 118 | °C | ISO 306 |
| Melting Temperature | 126 to 128 | °C |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss | 50 to 88 | ASTM D2457 | |
| Haze | 3.0 to 18 | % | ASTM D1003 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Shandong PA610 Type I | Shandong Guangyin New Materials Co., Ltd. | Nylon 610 | Shandong PA610 |
| Edgetek™ PC-20GF/000 MR BK017 | PolyOne Corporation | PC | Edgetek™ |
| I. Stern HP-8250 | I. STERN & CO. INC. | PS (HIPS) | I. Stern |
| Karina RED PVC COMPOUND 809D42/ 7-C-IS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| AXLENE® 2RM | INDELPRO, S.A. de C.V. | PP Random Copolymer | AXLENE® |