Plenco 05118 (Compression)
| Category: | Phenolic , Phenolic |
| Manufacturer: | Plastics Engineering Co. |
| Trademark: | Plenco |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 0ZWBZK_Plenco-05118-Compression-.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PLENCO 05118 is a mineral and graphite filled phenolic molding compound, formulated for bearing seals. 05118 provides for a low coefficient of friction, abrasion resistance, minimal water absorption, and excellent dimensional stability under severe exposure. 05118 is available in gray. 05118 is not recommended for electrical insulating applications. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.81 | g/cm³ | ASTM D792 |
| Apparent Density | 0.87 | g/cm³ | ASTM D1895 |
| Molding Shrinkage - Flow | 0.19 | % | ASTM D955 |
| Water Absorption (24 hr) | 0.050 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (E-Scale) | 59 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 12000 | MPa | ASTM D638 |
| Tensile Strength | 32.0 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 0.40 | % | ASTM D638 |
| Flexural Modulus | 9890 | MPa | ASTM D790 |
| Flexural Strength | 54.7 | MPa | ASTM D790 |
| Compressive Strength | 134 | MPa | ASTM D695 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | 17.4 | J/m | ASTM D256 |
| Notched Izod Impact | 16 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 194 | °C | ASTM D648 |
| Continuous Use Temperature | 212 | °C | ASTM D794 |
| CLTE - Flow | 3.2E-5 | cm/cm/°C | ASTM E831 |
| Thermal Conductivity (100°C) | 1.2 | W/m/K | ASTM C177 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Oxygen Index | 43 | % | ASTM D2863 |
| Additional Information |
|---|
| The value listed as Thermal Conductivity, ASTM C177 was tested according to the ASTM E1461 standard.The value listed as Mold Shrink, Linear-Flow, ASTM D955 was tested according to the ASTM D6289 standard.Post Shrinkage, ASTM D6289, 72hr, 120°C: 0.06%Drop Ball Impact, PLENCO Method: 57 J/m |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 90.0 | °C | |
| Drying Time | 0.50 | hr | |
| Mold Temperature | 165 - 182 | °C | |
| Back Pressure | 0.300 | MPa | |
| Screw Speed | < 60 | rpm |
| Injection instructions |
|---|
| Mold Close Time: 3-8 sec |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TOTAL Polystyrene Crystal 1540 (EU) | TOTAL Refining & Chemicals | PS (GPPS) | TOTAL Polystyrene |
| HiFill® PP GF20 CC | Techmer Engineered Solutions | PP, Unspecified | HiFill® |
| Karina COMP. PVC IVORY -E 853-35/ 1-B-IS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Sylvin 8250-70 Grey 9578 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| NEOFLON™ AP-201SH | DAIKIN AMERICA, INC. | PFA | NEOFLON™ |