INSULCAST® 125/INSULCURE 9
| Category: | Epoxy , Epoxy; Epoxide |
| Manufacturer: | ITW Polymers Coatings North America |
| Trademark: | INSULCAST® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 0Z5Rlt_INSULCAST-125-INSULCURE-9.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| INSULCAST 125 is a low viscosity, general purpose potting and casting compound. The low viscosity enables it to be used in potting densely packed modules, thereby insuring good flow and penetration around components. INSULCAST 125 contains non-abrasive fillers and is suitable for automatic dispensing equipment. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Processing Method |
|
| Hardness | Nominal Value | Test Method | |
|---|---|---|---|
| Durometer Hardness (Shore D) | 80 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | 75.8 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 2.5 | % | ASTM D638 |
| Flexural Strength | 100 | MPa | ASTM D790 |
| Compressive Strength | 86.2 | MPa | ASTM D695 |
| Thermal | Nominal Value | Unit | |
|---|---|---|---|
| CLTE - Flow | 4.8E-5 | cm/cm/°C | |
| Thermal Conductivity | 0.65 | W/m/K | |
| Heat Deflection Temperature | 80 | °C | |
| Service Temperature | 105 | °C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 5.0E+14 | ohms·cm | ASTM D257 |
| Dielectric Strength | 16 | kV/mm | ASTM D149 |
| Dielectric Constant (1 kHz) | 4.20 | ASTM D150 | |
| Dissipation Factor (1 kHz) | 0.023 | ASTM D150 |
| Thermoset | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Thermoset Components | |||
| Hardener | Mix Ratio by Weight: 6.0 to 7.0 | ||
| Resin | Mix Ratio by Weight: 100 | ||
| Shelf Life (25°C) | 52 | wk |
| Uncured Properties | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Color | |||
| -- 1 | Amber | ||
| -- 2 | Black | ||
| Density | ASTM D1475 | ||
| -- 3 | 0.968 | g/cm³ | |
| -- 4 | 1.55 | g/cm³ | |
| Viscosity | |||
| -- 5 | 0.055 | Pa·s | |
| 25°C 6 | 3.0 | Pa·s | |
| -- 7 | 7.5 | Pa·s | |
| Curing Time (25°C) | 16 to 24 | hr | |
| Pot Life 8(25°C) | 60 | min |
| Note Message | |
|---|---|
| 1 . | INSULCURE 9 |
| 2 . | INSULCAST 125 |
| 3 . | INSULCURE 9 |
| 4 . | INSULCAST 125 |
| 5 . | INSULCURE 9 |
| 6 . | Mixed |
| 7 . | INSULCAST 125 |
| 8 . | 100 gram mass |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Pro-fax KF6100 | LyondellBasell Industries | PP Homopolymer | Pro-fax |
| ALTECH® PP-B C 2030/550 GF30 CP | ALBIS PLASTIC GmbH | PP Copolymer | ALTECH® PP-B |
| DOMAMID® 66G15ST | DOMO Engineering Plastics SPA | Nylon 66 | DOMAMID® |
| Elasthane™ 55D MR | DSM Biomedical Inc. | TPU-Polyether | Elasthane™ |
| INSPIRE™ 114 EU | Braskem Europe GmbH | PP, Unspecified | INSPIRE™ |