GAPEX® HP RPP20EV10HB
| Category: | PP Copolymer , Polypropylene Copolymer |
| Manufacturer: | Ferro Corporation |
| Trademark: | GAPEX® HP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 0YyTwi_GAPEX-HP-RPP20EV10HB.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
GAPEX®HP RPP20EV10HB is a polypropylene copolymer (PP Copoly) material, which contains a 20% glass fiber reinforced material. This product is available in North America, Africa and the Middle East, Latin America, Europe or Asia Pacific,. GAPEX®The main features of HP RPP20EV10HB are:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Appearance |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.06 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 4.0 | g/10 min | ASTM D1238 |
| Molding Shrinkage | ASTM D955 | ||
| Flow | 0.50 | % | ASTM D955 |
| Transverse flow | 0.90 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield, 23°C) | 64.1 | MPa | ASTM D638 |
| Tensile Elongation (Break, 23°C) | 4.5 | % | ASTM D638 |
| Flexural Modulus | ASTM D790 | ||
| 1% secant : 23°C | 3520 | MPa | ASTM D790 |
| Tangent : 23°C | 3690 | MPa | ASTM D790 |
| Flexural Strength (Yield, 23°C) | 100 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 120 | J/m | ASTM D256 |
| Unnotched Izod Impact (23°C) | 510 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, not annealed | 158 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 143 | °C | ASTM D648 |
| RTI Elec (1.50 mm) | 65.0 | °C | UL 746 |
| RTI Imp (1.50 mm) | 65.0 | °C | UL 746 |
| RTI (1.50 mm) | 65.0 | °C | UL 746 |
| Additional Information |
|---|
| Filler Content, ASTM D2584: 21% |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 71.1 - 82.2 | °C | |
| Drying Time | 2.0 - 4.0 | hr | |
| Rear Temperature | 221 - 238 | °C | |
| Middle Temperature | 227 - 243 | °C | |
| Front Temperature | 232 - 260 | °C | |
| Nozzle Temperature | 232 - 260 | °C | |
| Processing (Melt) Temp | 221 - 238 | °C | |
| Mold Temperature | 37.8 - 65.6 | °C | |
| Injection Rate | Slow-Moderate | ||
| Back Pressure | 0.138 - 0.345 | MPa | |
| Cushion | 5.08 - 12.7 | mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Shinko-Lac® ASA TA-20S | Mitsubishi Rayon America Inc. | ASA+PC | Shinko-Lac® |
| TRIMID® N6-G15L | Polymer Technology and Services, LLC | Nylon 6 | TRIMID® |
| BP Flex D 0850 (C) BLK | Buckeye Polymers, Inc. | TPE | BP Flex |
| Cellophane™ 350PS | Innovia Films Ltd. | Cellulose, Regenerated | Cellophane™ |
| SIBUR Synthetic Rubber SSBR-2560 Grade B | SIBUR | SBR, Solution | SIBUR Synthetic Rubber |