Amilan® CM3001R
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Toray Resin Company |
| Trademark: | Amilan® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 0YO4Zg_Amilan-CM3001R.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Amilan® CM3001R is a Polyamide 66 (Nylon 66) product filled with 40% mineral. It is available in Asia Pacific, Europe, or North America. Characteristics include:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Part Marking Code |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density (23°C) | 1.51 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage | Internal Method | |||
| Across Flow : 3.00 mm 1 | 1.0 to 1.4 | -- | % | |
| Flow : 3.00 mm 2 | 0.70 to 1.0 | -- | % | |
| Water Absorption | ISO 62 | |||
| 23°C, 24 hr | 0.60 | -- | % | |
| Saturation, 23°C | 5.1 | -- | % |
| Hardness | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Rockwell Hardness | ISO 2039-2 | |||
| M-Scale, 23°C | 83 | -- | ||
| R-Scale, 23°C | 120 | -- |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Stress | ISO 527-2 | |||
| -40°C | 120 | -- | MPa | |
| 23°C | 95.0 | 70.0 | MPa | |
| 80°C | 40.0 | -- | MPa | |
| Tensile Strain | ISO 527-2 | |||
| Break, -40°C | 3.0 | -- | % | |
| Break, 23°C | 3.5 | 5.0 | % | |
| Break, 80°C | 5.0 | -- | % | |
| Flexural Modulus | ISO 178 | |||
| -40°C | 6200 | -- | MPa | |
| 23°C | 5800 | 3000 | MPa | |
| 80°C | 2000 | -- | MPa | |
| Flexural Stress | ISO 178 | |||
| -40°C | 185 | -- | MPa | |
| 23°C | 155 | 100 | MPa | |
| 80°C | 65.0 | -- | MPa |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 5.5 | -- | kJ/m² | ISO 179 |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, Unannealed | 243 | -- | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 185 | -- | °C | ISO 75-2/A |
| Melting Temperature | 265 | -- | °C | DSC |
| Flammability | Dry | Conditioned | Test Method | |
|---|---|---|---|---|
| Flame Rating | HB | -- | UL 94 |
| Note Message | |
|---|---|
| 1 . | 80x80x3 |
| 2 . | 80x80x3mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RAMOFIN PPH343T4BK10-1 | Polyram Ram-On Industries | PP Homopolymer | RAMOFIN |
| RheTech Thermoplastic Polyolefin FT4702-698UV | RheTech, Inc. | Polyolefin, Unspecified | RheTech Thermoplastic Polyolefin |
| Teslin® SP 800 | PPG Industries, Inc. | PE, Unspecified | Teslin® |
| Braskem PE CP 191XP | Braskem | PP Copolymer | Braskem PE |
| Hylon® N2013L | Ravago Manufacturing Americas, LLC | Nylon 6 | Hylon® |