Generic PC+PET
| Category: | PC+PET , Polycarbonate + PET |
| Manufacturer: | Generic |
| Trademark: | Generic |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 0YIkFe_Generic-PC-PET.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
This data represents typical values that have been calculated from all products classified as: Generic PC+PET This information is provided for comparative purposes only. |
| General Information |
|---|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.20 - 1.22 | g/cm³ | ASTM D792 |
| 23°C | 1.20 - 1.34 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (265°C/5.0 kg) | 12 - 30 | g/10 min | ASTM D1238 |
| Molding Shrinkage | |||
| Flow : 23°C | 0.60 - 0.90 | % | ASTM D955 |
| 23°C | 0.40 - 0.80 | % | ISO 294-4 |
| Water Absorption | |||
| 23°C, 24 hr | 0.098 - 0.19 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 0.080 - 0.35 | % | ISO 62 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (23°C) | 110 - 119 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| 23°C | 1700 - 4600 | MPa | ASTM D638 |
| 23°C | 1950 - 4310 | MPa | ISO 527-2 |
| Tensile Strength | |||
| Yield, 23°C | 46.5 - 65.0 | MPa | ASTM D638 |
| Yield, 23°C | 49.4 - 67.5 | MPa | ISO 527-2 |
| Fracture, 23°C | 44.7 - 60.5 | MPa | ASTM D638 |
| Fracture, 23°C | 44.2 - 55.4 | MPa | ISO 527-2 |
| 23°C | 53.9 - 59.8 | MPa | ASTM D638 |
| Tensile Elongation | |||
| Yield, 23°C | 3.3 - 8.1 | % | ASTM D638 |
| Yield, 23°C | 3.6 - 5.0 | % | ISO 527-2 |
| Fracture, 23°C | 56 - 150 | % | ASTM D638 |
| Fracture, 23°C | 3.0 - 110 | % | ISO 527-2 |
| Flexural Modulus | |||
| 23°C | 1890 - 2540 | MPa | ASTM D790 |
| 23°C | 2110 - 4000 | MPa | ISO 178 |
| Flexural Strength | |||
| 23°C | 66.5 - 91.6 | MPa | ASTM D790 |
| 23°C | 65.0 - 98.0 | MPa | ISO 178 |
| Yield, 23°C | 86.0 - 104 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 8.0 - 56 | kJ/m² | ISO 179 |
| Notched Izod Impact | |||
| 23°C | 90 - 930 | J/m | ASTM D256 |
| 23°C | 8.6 - 51 | kJ/m² | ISO 180 |
| Instrumented Dart Impact (23°C) | 5.12 - 60.4 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, not annealed | 126 - 137 | °C | ASTM D648 |
| 0.45 MPa, not annealed | 120 - 132 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 73.9 - 131 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 94.5 - 120 | °C | ISO 75-2/A |
| Vicat Softening Temperature | |||
| -- | 137 - 155 | °C | ASTM D1525 |
| -- | 128 - 145 | °C | ISO 306 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 104 - 121 | °C | |
| Drying Time | 2.9 - 5.1 | hr | |
| Suggested Max Moisture | 0.019 - 0.020 | % | |
| Suggested Shot Size | 60 - 65 | % | |
| Rear Temperature | 235 - 262 | °C | |
| Middle Temperature | 254 - 267 | °C | |
| Front Temperature | 254 - 280 | °C | |
| Nozzle Temperature | 260 - 271 | °C | |
| Processing (Melt) Temp | 255 - 281 | °C | |
| Mold Temperature | 69.7 - 80.8 | °C | |
| Back Pressure | 0.259 - 1.50 | MPa | |
| Screw Speed | 36 - 80 | rpm |
| Injection instructions |
|---|
| This data represents typical values that have been calculated from all products classified as: Generic PC+PETThis information is provided for comparative purposes only. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTV-2 P-125 | Silicones, Inc. | Silicone Rubber, RTV-2 | RTV-2 |
| Tarnamid® T- 30 MHLS | Grupa Azoty S.A. | Nylon 6 | Tarnamid® |
| Unipren® Elastomers A3 NTLA010 35A EB06S1 UP329 | Petropol Industry and Trade of Polymers LTDA | TPE | Unipren® Elastomers |
| Borealis PP VG602 | Borealis AG | TPO | Borealis PP |
| Polifil® PP GFRMPPCC-30 | The Plastics Group | PP Impact Copolymer | Polifil® PP |