LNP™ LUBRICOMP™ OX96668 compound
| Category: | PPS, Linear , Linear Polyphenylene Sulfide |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ LUBRICOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 0XeEt6_LNP-LUBRICOMP-OX96668-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP LUBRICOMP OX96668 is a compound based on Linear PPS resin containing Proprietary Filler(s). Added feature of this material is: Wear Resistant. Also known as: LNP* LUBRICOMP* Compound PDX-O-96668 Product reorder name: OX96668 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.68 | g/cm³ | ASTM D792 |
| Molding Shrinkage | ASTM D955 | ||
| Flow : 24 hr | 0.10 to 0.30 | % | |
| Across Flow : 24 hr | 0.60 to 0.80 | % | |
| Water Absorption | |||
| 24 hr, 50% RH | 0.020 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 0.020 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 13600 | MPa | ASTM D638 |
| -- | 13000 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Break 2 | 131 | MPa | ASTM D638 |
| Break | 129 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Break 3 | 1.6 | % | ASTM D638 |
| Break | 1.5 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| 50.0 mm Span 4 | 11800 | MPa | ASTM D790 |
| -- 5 | 12200 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 188 | MPa | ISO 178 |
| Break, 50.0 mm Span 6 | 189 | MPa | ASTM D790 |
| Coefficient of Friction | ASTM D3702 Modified | ||
| vs. Itself - Dynamic | 0.45 | ||
| vs. Itself - Static | 0.72 | ||
| Wear Factor | ASTM D3702 Modified | ||
| Ring | 8.70 | 10^-10 in^5-min/ft-lb-hr | |
| Washer | 80.0 | 10^-10 in^5-min/ft-lb-hr |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 91 | J/m | ASTM D256 |
| 23°C 7 | 8.8 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 510 | J/m | ASTM D4812 |
| 23°C 8 | 32 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Total Energy | 12.1 | J | ASTM D3763 |
| -- | 3.92 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 277 | °C | ASTM D648 |
| 0.45 MPa, Unannealed, 64.0 mm Span 9 | 274 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed, 3.20 mm | 260 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 10 | 249 | °C | ISO 75-2/Af |
| CLTE | ASTM D696 | ||
| Flow : -30 to 30°C | 1.9E-5 | cm/cm/°C | |
| Transverse : -30 to 30°C | 4.2E-5 | cm/cm/°C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 to 149 | °C | |
| Drying Time | 4.0 | hr | |
| Rear Temperature | 304 to 316 | °C | |
| Middle Temperature | 321 to 332 | °C | |
| Front Temperature | 332 to 343 | °C | |
| Processing (Melt) Temp | 316 to 321 | °C | |
| Mold Temperature | 138 to 166 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | Type I, 5.0 mm/min |
| 3 . | Type I, 5.0 mm/min |
| 4 . | 1.3 mm/min |
| 5 . | 2.0 mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 80*10*4 |
| 8 . | 80*10*4 |
| 9 . | 80*10*4 mm |
| 10 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Prime PP PO 500 | Primex Plastics Corporation | PP Copolymer | Prime PP |
| RheTech Polypropylene T20P250-699UV | RheTech, Inc. | PP Copolymer | RheTech Polypropylene |
| SHIN-A SAP-6318XB35 | SHIN-A T&C | Acrylic, Unspecified | SHIN-A |
| Niplene F20 AGR | Soredi S.p.a. | PP Homopolymer | Niplene |
| Karina CRYSTAL PVC COMPOUND -E 802-IS-SD | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |