Sindustris PP TE5109H
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | Sincerity Australia Pty Ltd. |
| Trademark: | Sindustris PP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 0XcXpY_Sindustris-PP-TE5109H.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Sindustris PP TE5109H is a Polypropylene material filled with mineral. It is available in Asia Pacific for injection molding. Important attributes of Sindustris PP TE5109H are:
Typical application of Sindustris PP TE5109H: Automotive |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| UL File Number |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.960 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 19 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (3.20 mm) | 0.90 to 1.0 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Yield, 3.20 mm) | 14.7 | MPa | ASTM D638 |
| Tensile Elongation 2(Break, 3.20 mm) | 300 | % | ASTM D638 |
| Flexural Modulus 3(6.40 mm) | 1080 | MPa | ASTM D790 |
| Flexural Strength 4(6.40 mm) | 19.6 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ASTM D256 | ||
| -10°C, 6.40 mm | 78 | J/m | |
| 23°C, 6.40 mm | 490 | J/m |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed, 3.20 mm) | 115 | °C | ASTM D648 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 70.0 to 80.0 | °C | |
| Drying Time | 3.0 to 4.0 | hr | |
| Suggested Max Moisture | 0.010 | % | |
| Rear Temperature | 190 to 210 | °C | |
| Middle Temperature | 200 to 230 | °C | |
| Front Temperature | 200 to 230 | °C | |
| Nozzle Temperature | 210 to 230 | °C | |
| Processing (Melt) Temp | 200 to 230 | °C | |
| Mold Temperature | 40.0 to 60.0 | °C | |
| Back Pressure | 29.4 to 58.8 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| 3 . | 10 mm/min |
| 4 . | 10 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Nipol® DN3335 | Zeon Chemicals L.P. | NBR | Nipol® |
| Adell PP EF-12 | Adell Plastics, Inc. | PP, Unspecified | Adell PP |
| Starflam RF0067K | Eurostar Engineering Plastics | Nylon 66 | Starflam |
| LG EVA EP28025 | LG Chem Ltd. | EVA | LG EVA |
| LNP™ LUBRICOMP™ RCL34 compound | SABIC Innovative Plastics Europe | Nylon 66 | LNP™ LUBRICOMP™ |