4LEX® 10F10000
| Category: | PC , Polycarbonate |
| Manufacturer: | 4Plas |
| Trademark: | 4LEX® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 0Wzvhv_4LEX-10F10000.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 4LEX 10F10000 is a MFI 10 to 14 Unfilled Polycarbonate |
| General Information | |
|---|---|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.24 | g/cm³ | ISO 1183 |
| Molding Shrinkage | 0.50 | % | ISO 2557 |
| Water Absorption 1(Equilibrium, 23°C, 50% RH) | 0.15 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 2350 | MPa | ISO 527-2/5 |
| Tensile Stress | ISO 527-2/5 | ||
| Yield, 23°C | 58.0 | MPa | ISO 527-2/5 |
| Fracture, 23°C | 52.0 | MPa | ISO 527-2/5 |
| Tensile Strain | ISO 527-2/5 | ||
| Yield, 23°C | 8.0 | % | ISO 527-2/5 |
| Fracture, 23°C | 93 | % | ISO 527-2/5 |
| Flexural Modulus 2(23°C) | 2200 | MPa | ISO 178 |
| Flexural Stress | 90.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 19 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact | ISO 180/1A | ||
| -30°C | 15 | kJ/m² | ISO 180/1A |
| 23°C | 60 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength (23°C) | No Break | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (0.45 MPa, Unannealed) | 144 | °C | ISO 75-2/B |
| Vicat Softening Temperature | 145 | °C | ISO 306/B |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Comparative Tracking Index | 200 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.60 mm) | HB | UL 94 | |
| Glow Wire Flammability Index (2.00 mm) | 870 | °C | IEC 60695-2-12 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 120 | °C | |
| Drying Time | 3.0 - 4.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Processing (Melt) Temp | 260 - 300 | °C | |
| Mold Temperature | 80.0 - 100 | °C | |
| Injection Rate | Moderate-Fast | ||
| Holding Pressure | 60.0 - 120 | MPa | |
| Screw Speed | 200 | rpm |
| Injection instructions |
|---|
| Feed Throat Temperature: 60 - 80 °CBack Pressure: Low |
| Note Message | |
|---|---|
| 1 . | 24 Hrs |
| 2 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| NEFTEKHIM PE 6152C (526H3) | Nizhnekamskneftekhim Inc. | HDPE | NEFTEKHIM PE |
| Innoprene 1550N/B | Kumho Polychem Co., Ltd. | TPV | Innoprene |
| Petroquim PP PH 2615 | Petroquim S.A. | PP Homopolymer | Petroquim PP |
| Plaslube® HTN 01410 BK | Techmer Engineered Solutions | Nylon, Unspecified | Plaslube® |
| Thermec N™ 4340CF20 | Technical Polymers, LLC | PPA | Thermec N™ |