High Density Polyethylene Copolymer 1-hexene Extrusion-Blow Molding

Applications

Bottles for home use chemical liquid substances (bleache) and industrial chemicals (lubricants) up to 10 litters.

Bottles containing liquids for personal use (shampoo). Bottles for pharmaceutical products.

Characterisitics

The KPOL® resin meets the requirements of section 177.1520, paragraph C, from chapter 21 denominated "Olefin Polymers" from the Code of Federal Regulations of the FDA, to be utilized with direct food contact.

General Information
Additive	Antioxidant
Features	Antioxidant Copolymer Food Contact Acceptable Hexene Comonomer High Density
Uses	Bottles
Agency Ratings	FDA 21 CFR 177.1520
Forms	Pellets
Processing Method	Extrusion Blow Molding

Physical	Nominal Value	Unit	Test Method
Density	0.955	g/cm³	ASTM D1505
Melt Mass-Flow Rate (MFR) (190°C/2.16 kg)	0.35	g/10 min	ASTM D1238
Environmental Stress-Cracking Resistance
Condition B, 60°C, 10% Igepal CO-630, F50 ¹	> 500	hr	ASTM D2561
50°C, 3.18 mm, 100% Igepal CO-630, F50 ²	45.0	hr	ASTM D1693A
50°C, 1.91 mm, 100% Igepal CO-630, F50 ³	35.0	hr	ASTM D1693B

Hardness	Nominal Value	Unit	Test Method
Durometer Hardness (Shore D, 1 sec, 23°C)	67		ASTM D2240

Mechanical	Nominal Value	Unit	Test Method
Tensile Strength ⁴(Yield)	27.6	MPa	ASTM D638
Tensile Elongation ⁵(Break)	600	%	ASTM D638
Flexural Modulus - Tangent ⁶(3.20 mm)	1380	MPa	ASTM D790

Impact	Nominal Value	Unit	Test Method
Notched Izod Impact (3.20 mm)	270	J/m	ASTM D256A
Tensile Impact Strength	242	kJ/m²	ASTM D1822

Thermal	Nominal Value	Unit	Test Method
Deflection Temperature Under Load (0.45 MPa, Unannealed)	76.0	°C	ASTM D648
Brittleness Temperature ⁷	< -75.0	°C	ASTM D746A
Vicat Softening Temperature	127	°C	ASTM D1525 ⁸
Melting Temperature	129	°C	DSC

Note Message
1 .	16 oz cylindrical bottle (approximated mass of 20 g) filled up to 33% of its capacity
2 .	Grooved Specimen
3 .	Grooved Specimen
4 .	Type IV, 50 mm/min
5 .	Type IV, 50 mm/min
6 .	13 mm/min
7 .	F50; 25 lbfXin
8 .	Rate A (50°C/h), Loading 1 (10 N)

Resin Grade	Manufacturer	Category	Trademark
Quantum Composites QC-8816	Quantum Composites Inc.	Vinyl Ester	Quantum Composites
MIDILENA III HDPE6205B	ROMPETROL PETROCHEMICALS S.R.L.	HDPE	MIDILENA III
Sindustris PC SR3109L	Sincerity Australia Pty Ltd.	PC	Sindustris PC
Sylvin 8409-65UV Natural	Sylvin Technologies Incorporated	PVC+PUR	Sylvin
Vistamaxx™ 3588FL	ExxonMobil Chemical	PP Elastomer	Vistamaxx™