Rilsamid® AESNO P40 TL
| Category: | Nylon 12 , Polyamide 12 |
| Manufacturer: | Arkema |
| Trademark: | Rilsamid® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 0Vt5wc_Rilsamid-AESNO-P40-TL.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Rilsamid ® AESNO P40 TL is a natural polyamide. This grade is plasticized and designed for tube extrusion. AESNO P40 TL falls into the PA12-PHL category according to DIN 73378. MAIN APPLICATIONS
|
| General Information | |
|---|---|
| Additive |
|
| Uses |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.03 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (235°C/5.0 kg) | 16.0 | cm³/10min | ISO 11357 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness | ISO 868 | ||
| Shore D | 71 | ||
| Shore D, 15 sec | 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 380 | MPa | ISO 527-2 |
| Tensile Stress | ISO 527-2 | ||
| Yield | 23.0 | MPa | |
| Break | 52.0 | MPa | |
| Tensile Strain | ISO 527-2 | ||
| Yield | 25 | % | |
| Break | > 200 | % | |
| Flexural Modulus | 350 to 450 | MPa | ISO 178 |
| Taber Abrasion Resistance (1000 Cycles, 1000 g, CS-17 Wheel) | 6.00 | mg | ISO 9352 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | ||
| -30°C | 5.0 | kJ/m² | |
| 23°C | No Break | ||
| Charpy Unnotched Impact Strength | ISO 179 | ||
| -30°C | No Break | ||
| 23°C | No Break |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melting Temperature | 175 | °C | ISO 11357-3 |
| Additional Information | Nominal Value | Test Method | |
|---|---|---|---|
| ISO Shortname | PA12-P, EHL, 22-004 | ISO 1874 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 4.0 to 6.0 | hr | |
| Melt Temperature | 210 to 260 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Ultramid® A3WGM33 BK20560 | BASF Corporation | Nylon 66 | Ultramid® |
| Bynel® 30E671 | DuPont Packaging & Industrial Polymers | EVA | Bynel® |
| GERMAFORM 9 MF 10 | Kunststoff-Kontor-Hamburg GmbH | Acetal (POM) Copolymer | GERMAFORM |
| Hanwha Total PP BI392 | HANWHA TOTAL PETROCHEMICALS Co., Ltd. | PP, Unspecified | Hanwha Total PP |
| LNP™ STAT-KON™ PD000 compound | SABIC Innovative Plastics Europe | Nylon 6 | LNP™ STAT-KON™ |