MAJORIS BG384
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | AD majoris |
| Trademark: | MAJORIS |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 0ViLiC_MAJORIS-BG384.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
BG384 is a 30% chemically coupled glass fibre reinforced polypropylene compound intended for injection moulding and extrusion profiles . The product is available in natural, but other colours can be provided on request. BG384 has been developed especially for demanding applications in various engineering sectors. BG384 has high rigidity and good impact strength, good dimensional stability and good creep resistancy also at high temperatures. APPLICATIONS Product requiring very high overall mechanical performance such as:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.12 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 1.0 | g/10 min | ISO 1133 |
| Molding Shrinkage (2.00 mm) | 0.60 - 0.90 | % | Internal method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Yield) | 65.0 | MPa | ISO 527-2/50 |
| Tensile Strain (Yield) | 3.3 | % | ISO 527-2/50 |
| Flexural Modulus | 4500 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -20°C | 13 | kJ/m² | ISO 179/1eA |
| 23°C | 20 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact | ISO 180/1A | ||
| -20°C | 16 | kJ/m² | ISO 180/1A |
| 23°C | 21 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 148 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 132 | °C | ISO 75-2/A |
| Vicat Softening Temperature | |||
| -- | 153 | °C | ISO 306/A |
| -- | 122 | °C | ISO 306/B |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Processing (Melt) Temp | 210 - 250 | °C | |
| Mold Temperature | 30.0 - 70.0 | °C | |
| Injection Rate | Slow-Moderate |
| Injection instructions |
|---|
| Holding pressure: 50 to 70% of the injection pressure |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 285H TFE 13 SI 2 | RTP Company | Nylon 66 | RTP |
| VITAMIDE® AI10BK6201CT | Jackdaw Polymers | Nylon 66 | VITAMIDE® |
| Nypel® 2314 HS BK6 | BASF Corporation | Nylon 6 | Nypel® |
| Kingfa HG-172 | Kingfa | PP, Unspecified | Kingfa |
| LG PVC LP170G | LG Chem Ltd. | PVC Homopolymer | LG PVC |