LNP™ THERMOCOMP™ DF006 compound
| Category: | PC , Polycarbonate |
| Manufacturer: | SABIC Innovative Plastics Asia Pacific |
| Trademark: | LNP™ THERMOCOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 0VYmGt_LNPTHERMOCOMPDF006compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP THERMOCOMP DF006 is a compound based on Polycarbonate resin containing 30% Glass Fiber. Also known as: LNP* THERMOCOMP* Compound DF-1006 Product reorder name: DF006 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.45 | g/cm³ | ASTM D792, ISO 1183 |
| -- | 1.44 | g/cm³ | ASTM D792 |
| Water Absorption | |||
| 24 hr, 50% RH | 0.070 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 0.070 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1 | 8640 | MPa | ASTM D638 |
| Tensile Strength | |||
| Fracture 2 | 114 | MPa | ASTM D638 |
| Fracture | 114 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Yield 3 | 2.7 | % | ASTM D638 |
| Fracture 4 | 3.2 | % | ASTM D638 |
| Fracture | 7.5 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| 50.0mm span 5 | 8230 | MPa | ASTM D790 |
| -- 6 | 7870 | MPa | ISO 178 |
| Flexural Strength 7(Break, 50.0 mm Span) | 149 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 140 | J/m | ASTM D256 |
| 23°C 8 | 14 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 910 | J/m | ASTM D4812 |
| 23°C 9 | 57 | kJ/m² | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, unannealed, 3.20mm | 144 | °C | ASTM D648 |
| 0.45 MPa, unannealed, 64.0mm span 10 | 145 | °C | ISO 75-2/Bf |
| 1.8 MPa, unannealed, 3.20mm | 140 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 64.0mm span 11 | 141 | °C | ISO 75-2/Af |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Rear Temperature | 293 - 304 | °C | |
| Middle Temperature | 310 - 321 | °C | |
| Front Temperature | 321 - 332 | °C | |
| Processing (Melt) Temp | 304 - 327 | °C | |
| Mold Temperature | 82.2 - 110 | °C | |
| Back Pressure | 0.172 - 0.344 | MPa | |
| Screw Speed | 30 - 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | Type 1, 5.0 mm/min |
| 3 . | Type 1, 5.0 mm/min |
| 4 . | Type 1, 5.0 mm/min |
| 5 . | 1.3 mm/min |
| 6 . | 2.0 mm/min |
| 7 . | 1.3 mm/min |
| 8 . | 80*10*4 |
| 9 . | 80*10*4 |
| 10 . | 80*10*4 mm |
| 11 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Shuman PC 980-05V0 | Shuman Plastics, Inc. | PC | Shuman PC |
| Sumikon® FM-MK205 | Sumitomo Bakelite Co., Ltd. | PPS | Sumikon® |
| Acculam™ Phenolkraft Paper XX/XXX | Accurate Plastics, Inc. | Phenolic | Acculam™ |
| COSMOPLENE® W331 | TPC, The Polyolefin Company (Singapore) Pte Ltd | PP Random Copolymer | COSMOPLENE® |
| Panlite® G-3110PH | TEIJIN LIMITED | PC | Panlite® |