UNITHENE® LH606-13
| Category: | HDPE , High Density Polyethylene |
| Manufacturer: | USI Corporation |
| Trademark: | UNITHENE® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 0UlFg5_UNITHENE-LH606-13.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
UNITHENE LH606-13 is a high density polyethylene (HDPE) suitably used for injection molding. The product used outdoors could stand age because containing UV absorber. Typical applications are the injection molding of beer crates, fruit crates, food containers, other industrial items such as pallets, transportation crate. UNITHENE LH606-13 possesses excellent weatherability, high impact strength, good resistance to stress cracking, good stiffness, high hardness, good surface gloss, less warpage, low shrinkage, good processability. UNITHENE LH606-13 can be easily pigmented to any color by either dry blending or melt blending of the pigment into the resin.Printing on items molded from UNITHENE LH606-13 can be easily accomplished after a simple flame, chemical or electronic surface treatment. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.962 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) | 6.0 | g/10 min | ASTM D1238 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 69 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus - 1% Secant (Compression Molded) | 981 | MPa | ASTM D638 |
| Tensile Strength | ASTM D638 | ||
| Yield | 31.4 | MPa | ASTM D638 |
| Fracture | 21.6 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 620 | % | ASTM D638 |
| Apparent Bending Modulus | 971 | MPa | ASTM D747 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 69 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Brittleness Temperature | < -76.0 | °C | ASTM D746 |
| Vicat Softening Temperature | 127 | °C | ASTM D1525 |
| Peak Melting Temperature | 135 | °C | ASTM D3418 |
| Additional Information |
|---|
| Torsional Stiffness, ASTM D1043: 12500 kg/cm² |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sylvin 2990-90 Clear | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| DENILEN B 5010 CB | Vamp Tech | PP, Unspecified | DENILEN |
| Escorene™ Ultra UL 12530CC | ExxonMobil Chemical | EVA | Escorene™ Ultra |
| Hifax TYC 337P | LyondellBasell Industries | Polyolefin, Unspecified | Hifax |
| PENTAMID B GK30 H natur | PENTAC Polymer GmbH | Nylon 6 | PENTAMID B |