RALUPOL® UP 5000
| Category: | Polyester, TS , Thermoset Polyester |
| Manufacturer: | RASCHIG GmbH |
| Trademark: | RALUPOL® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 0Tibui_RALUPOL-UP-5000.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Glass-fibre reinforced Polyester moulding compound Low mould shrinkage and post-shrinkage, very good electrical values, excellent heat resistance, good mechanical strength Primary application(s): Commutators This product meets the allowed upper limits for heavy metals and PCAs and also conforms to the requirements of the EU directives 2002/95 (RoHS), 2002/96 (WEEE) and 2006/122 (PFOS) |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.95 to 2.15 | g/cm³ | ISO 1183 |
| Apparent Density | 0.80 to 1.00 | g/cm³ | ISO 60 |
| Molding Shrinkage - Flow 1 | 0.20 to 0.30 | % | ISO 2577 |
| Water Absorption (23°C, 24 hr) | < 0.50 | % | ISO 62 |
| Post Shrinkage 2 | < 0.10 | % | ISO 2577 |
| Additional Information | Nominal Value | Unit | |
|---|---|---|---|
| Compression Molding Molding Pressure | > 10.0 | MPa | |
| Compression Molding Temperature | 165 to 180 | °C |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (Compression Molded) | 9000 to 11000 | MPa | ISO 527-2 |
| Tensile Stress (Compression Molded) | 35.0 to 60.0 | MPa | ISO 527-2 |
| Flexural Modulus (Compression Molded) | 12000 to 15000 | MPa | ISO 178 |
| Flexural Stress (Compression Molded) | 85.0 to 130 | MPa | ISO 178 |
| Compressive Stress | 150 to 200 | MPa | ISO 604 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (Compression Molded) | 2.5 to 3.5 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (Compression Molded) | 4.0 to 6.0 | kJ/m² | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (8.0 MPa, Unannealed) | 180 to 200 | °C | ISO 75-2/C |
| CLTE - Flow (50 to 100°C) | 1.0E-5 to 2.0E-5 | cm/cm/°C | ISO 11359-2 |
| Thermal Conductivity | 0.60 to 0.70 | W/m/K | ASTM E1461 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+11 to 1.0E+12 | ohms | IEC 60093 |
| Volume Resistivity | > 1.0E+13 | ohms·cm | IEC 60093 |
| Electric Strength | 25 to 35 | kV/mm | IEC 60243-1 |
| Relative Permittivity | IEC 60250 | ||
| 100 Hz | 6.00 5.00 | ||
| 1 MHz | 5.00 4.00 | ||
| Dissipation Factor | IEC 60250 | ||
| 100 Hz | 0.010 to 0.030 | ||
| 1 MHz | 0.010 to 0.030 | ||
| Arc Resistance | PLC 4 | ASTM D495 | |
| Comparative Tracking Index | > 600 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.60 mm, Tested by RASCHIG) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Middle Temperature | 50.0 to 70.0 | °C | |
| Front Temperature | 80.0 to 100 | °C | |
| Processing (Melt) Temp | 100 to 115 | °C | |
| Mold Temperature | 165 to 180 | °C | |
| Back Pressure | 1.00 to 1.50 | MPa | |
| Screw Speed | 70 to 100 | rpm |
| Note Message | |
|---|---|
| 1 . | Compression Molded |
| 2 . | 168 h / 110°C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SLOVAMID® 6 GF 15 T 25 LTS | Plastcom | Nylon 6 | SLOVAMID® 6 |
| TRANSMARE® 22CGF30-0.001 | Transmare Compounding B.V. | PP Copolymer | TRANSMARE® |
| TRIREX® 3026B(R) | Samyang Corporation | PC | TRIREX® |
| K-Flex 3350 OR | Technovinyl Polymers India Ltd. | PVC Elastomer | K-Flex |
| SABIC® PPcompound G3230A | Saudi Basic Industries Corporation (SABIC) | PP, Unspecified | SABIC® PPcompound |