CYREX® 200-8005

Category:	PC+Acrylic , Polycarbonate + Acrylic (PMMA)
Manufacturer:	Evonik Cyro LLC
Trademark:	CYREX®
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	0TCgLH_CYREX-200-8005.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

WECHAT

Message

CYREX 200-8005 alloy is an opaque, acrylic polycarbonate alloy with an impact strength that is higher than polycarbonate for molding and extrusion medical applications.

Typical properties of CYREX® acrylic-polycarbonate alloys are:

outstanding impact strength and toughness

excellent processing characteristics

very good chemical resistance

good heat resistance

The special properties of CYREX 200-8005 alloy are:

medium melt flow rate

excellent resistance to both alcohol and lipids

good resistance to EtO, gamma and E-beam sterilization

Used for injection molding and extrusion of both thin and thick wall applications which require excellent toughness.

General Information
Features	Alcohol Resistant E-beam Sterilizable Ethylene Oxide Sterilizable Good Chemical Resistance Good Processability Good Toughness High Impact Resistance Medium Flow Medium Heat Resistance Radiation Sterilizable
Uses	Medical/Healthcare Applications Thick-walled Parts Thin-walled Parts
Agency Ratings	EC 1907/2006 (REACH) FDA 21 CFR 176.170 USP Class VI
Appearance	Opaque
Forms	Pellets
Processing Method	Extrusion Injection Molding

Physical	Nominal Value	Unit	Test Method
Specific Gravity	1.15	g/cm³	ASTM D792
Apparent Density	0.65	g/cm³	ASTM D1895
Melt Mass-Flow Rate (MFR) (230°C/3.8 kg)	3.5	g/10 min	ASTM D1238
Molding Shrinkage - Flow	0.40 to 0.80	%	ASTM D551
Water Absorption (24 hr)	< 0.26	%	ASTM D570

Hardness	Nominal Value	Unit	Test Method
Rockwell Hardness (M-Scale)	49		ASTM D785

Mechanical	Nominal Value	Unit	Test Method
Tensile Modulus	2210	MPa	ASTM D638
Tensile Strength (Yield)	55.2	MPa	ASTM D638
Tensile Elongation			ASTM D638
Yield	4.3	%
Break	57	%
Flexural Modulus	2210	MPa	ASTM D790
Flexural Strength	77.9	MPa	ASTM D790

Impact	Nominal Value	Unit	Test Method
Notched Izod Impact (23°C, 3.18 mm)	1400	J/m	ASTM D256

Thermal	Nominal Value	Unit	Test Method
Deflection Temperature Under Load (1.8 MPa, Annealed)	101	°C	ASTM D648
Vicat Softening Temperature	141	°C	ASTM D1525
CLTE - Flow (0 to 100°C)	9.4E-5	cm/cm/°C	ASTM D696

Optical	Nominal Value		Test Method
Transmittance	Opaque		ASTM D1003

Injection	Nominal Value	Unit
Drying Temperature	82.2	°C
Drying Time	3.0 to 4.0	hr
Rear Temperature	199 to 266	°C
Middle Temperature	199 to 266	°C
Front Temperature	199 to 266	°C
Processing (Melt) Temp	238 to 266	°C
Mold Temperature	65.6 to 98.9	°C

Resin Grade	Manufacturer	Category	Trademark
RTP 100 GB 40	RTP Company	PP, Unspecified	RTP
UBESTA 3014U	UBE Industries, Ltd.	Nylon 12	UBESTA
Bayblend® T88 GF-30	Covestro - Polycarbonates	PC+SAN	Bayblend®
Eltex® PF6220KJ	INEOS Olefins & Polymers Europe	mLLDPE	Eltex®
Kinta FR5500-001	Kinta Technology (Hong Kong) Co., Ltd.	PC+ABS	Kinta