Capran® 1200 Matte
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | Honeywell |
| Trademark: | Capran® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 0SuYZb_Capran-1200-Matte.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| CAPRAN® 1200 Matte is a nominal 0.55 mil (14 micron) biaxially oriented nylon 6 film with a matte appearance on one side. The matte surface imparts excellent contact clarity while maintaining superior scuff resistance. The combination of properties makes this film well suited for use in thermal lamination films designed for book cover applications. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Coefficient of Friction | ASTM D1894 | ||
| With Metal-Dynamic | 0.45 | ASTM D1894 | |
| With self-dynamics | 0.65 | ASTM D1894 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 14 | µm | |
| secant modulus | ASTM D882 | ||
| MD : 14 µm | 3100 | MPa | ASTM D882 |
| TD : 14 µm | 3100 | MPa | ASTM D882 |
| Tensile Strength | ASTM D882 | ||
| MD : Broken, 14 µm | 234 | MPa | ASTM D882 |
| TD : Broken, 14 µm | 234 | MPa | ASTM D882 |
| Tensile Elongation | ASTM D882 | ||
| MD : Broken, 14 µm | 83 | % | ASTM D882 |
| TD : Fracture | 83 | % | ASTM D882 |
| Optical | Nominal Value | Test Method | |
|---|---|---|---|
| Gloss (60°, 14.0 µm) | 7 - 9 | ASTM D2457 |
| Additional Information |
|---|
| Yield: 43300 in²/lbTensile Strength @ Break, ASTM D 882, MD: 28000 to 40000 psiTensile Strength @ Break, ASTM D 882, TD: 28000 to 40000 psiElongation @ Break, ASTM 882, MD: 65 to 100%Elongation @ Break, ASTM 882, TD: 65 to 100%Secant Modulus, ASTM D 882, MD: 375000 to 500000 psiSecant Modulus, ASTM D 882, TD: 375000 to 500000 psiGraves Tear (initial), ASTM D 1004, MD: 1000 to1300 g/milGraves Tear (initial), ASTM D 1004, TD: 1000 to1300 g/milCoefficient of Friction, ASTM D 1894: 0.50 to 0.60 vs Itself-DynamicCoefficient of Friction, ASTM D 1894: 0.40 to 0.50 vs Metal-DynamicSurface Tension, ASTM D5946, untreated side: >50 dynes/cmDimensional Stability, ASTM D1204, MD, 320°F, 5min: 1.0 to 2.0% shrinkageDimensional Stability, ASTM D1204, TD, 320°F, 5min: 0 to 0.5% shrinkagePuncture Strength, ASTM D1306: 925 g |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sylvin 2924-65 White 1500 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| VITAMIDE® BT33 ST | A. Schulman Europe | Nylon 6 | VITAMIDE® |
| UBE Polyethylene F222NH | UBE America, Inc. | PE, Unspecified | UBE Polyethylene |
| Nivionplast® B R356G NERO | SO.F.TER. SPA | Nylon 6 | Nivionplast® B |
| POLYFLAM® RIPP 374 ND CS1 | A. Schulman Europe | PP Copolymer | POLYFLAM® |