Ceramer 20
| Category: | PPSU , Polyphenylsulfone |
| Manufacturer: | Ceramer GmbH |
| Trademark: | Ceramer |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 0SL95L_Ceramer-20.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Ceramer and Ceramerplus are high performance polymers and additives based on polyphenylene sulfone (PPSO2). Ceramer and Ceramerplus have excellent thermal stability, inherent flame resistance and universal chemical resistance. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | |
|---|---|---|---|
| Density | 1.44 | g/cm³ | |
| Crystallinity | 60 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strain | ISO 178 | ||
| Break, -30°C | 2.1 | % | |
| Break, 23°C | 2.1 | % | |
| Break, 100°C | 1.9 | % | |
| Break, 200°C | 1.6 | % | |
| Break, 300°C | 2.8 | % | |
| Flexural Modulus | ISO 178 | ||
| -30°C | 3960 | MPa | |
| 23°C | 3850 | MPa | |
| 100°C | 3410 | MPa | |
| 200°C | 3030 | MPa | |
| 300°C | 1740 | MPa | |
| Flexural Stress | ISO 178 | ||
| -30°C | 87.0 | MPa | |
| 23°C | 84.0 | MPa | |
| 100°C | 65.0 | MPa | |
| 200°C | 47.0 | MPa | |
| 300°C | 43.0 | MPa |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 1.8 MPa, Unannealed | > 295 | °C | ISO 75-2/A |
| 8.0 MPa, Unannealed | 250 | °C | ISO 75-2/C |
| Glass Transition Temperature | 360 | °C | |
| CLTE - Flow | |||
| -50 to 100°C | 4.9E-5 | cm/cm/°C | |
| 100 to 200°C | 2.6E-5 | cm/cm/°C | |
| 200 to 300°C | 2.5E-5 | cm/cm/°C | |
| 300 to 360°C | 2.2E-5 | cm/cm/°C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+11 | ohms | ASTM D257 |
| Volume Resistivity | 1.0E+15 | ohms·cm | ASTM D257 |
| Dielectric Strength | 12 | kV/mm | ASTM D149 |
| Dielectric Constant | ASTM D150 | ||
| 1 kHz | 3.60 | ||
| 10 kHz | 3.50 | ||
| 100 kHz | 3.50 | ||
| 1 MHz | 3.41 | ||
| 10 MHz | 3.39 | ||
| 500 MHz | 3.37 | ||
| 1.00 GHz | 3.37 | ||
| 10.0 GHz | 3.28 | ||
| Dissipation Factor | ASTM D150 | ||
| 10 kHz | 2.0E-3 | ||
| 100 kHz | 4.0E-3 | ||
| 1 MHz | 5.9E-3 | ||
| 10 MHz | 5.2E-3 | ||
| 500 MHz | 5.4E-3 | ||
| 1.00 GHz | 5.8E-3 | ||
| 10.0 GHz | 9.5E-3 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SABIC® STAMAX 30YM240E | Saudi Basic Industries Corporation (SABIC) | PP, Unspecified | SABIC® STAMAX |
| Staramide AG6ST01 | Eurostar Engineering Plastics | Nylon 66 | Staramide |
| Colorite SF 6011SF | Colorite Polymers | PVC, Unspecified | Colorite SF |
| Dynaprene® VE1064A | Nantex Industry Co., Ltd. | TPE | Dynaprene® |
| EnviroPro 1020GF10 | West Michigan Compounding | PP Copolymer | EnviroPro |