Torlon® 4435
| Category: | PAI , Polyamide-imide |
| Manufacturer: | Solvay Specialty Polymers |
| Trademark: | Torlon® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 0SKWwf_Torlon-4435.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
Torlon 4435 polyamide-imide resin is specially developed for non-lubricating products with very low friction resistance in high pressure and high speed (PV) environments. Torlon 4435 is not only especially suitable for products that cannot be lubricated or do not need lubrication, but also provides additional safety margin for lubrication systems that have lost lubricating oil. The material has outstanding bending strength and compressive rigidity ranging from low temperature to high temperature, and can be used for products that need to bear weight. The coefficient of thermal expansion is low and has the ability to meet tight tolerance requirements in a wide temperature range. Due to its electrical dissipation characteristics, this brand can also be considered for anti-static purposes. Torlon 4435 can be specifically used for thrust washers, sealing rings, sliding blades, spools, bushings, clutch rollers and pistons. It can be injection molded into complex shapes.
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.59 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | 0.14 | % | ASTM D955 |
| Water Absorption (24 hr) | 0.12 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- | 9720 | MPa | ASTM D1708 |
| -- | 14500 | MPa | ASTM D638 |
| Tensile Strength | 93.8 | MPa | ASTM D638 |
| Tensile Stress | 110 | MPa | ASTM D1708 |
| Tensile Elongation | |||
| Fracture 1 | 6.0 | % | ASTM D1708 |
| Fracture | 1.0 | % | ASTM D638 |
| Flexural Modulus | ASTM D790 | ||
| 23°C | 14500 | MPa | ASTM D790 |
| 232°C | 10300 | MPa | ASTM D790 |
| Flexural Strength | ASTM D790 | ||
| 23°C | 152 | MPa | ASTM D790 |
| 232°C | 89.6 | MPa | ASTM D790 |
| Compressive Modulus | 8550 | MPa | ASTM D695 |
| Compressive Strength | 138 | MPa | ASTM D695 |
| Poisson's Ratio | 0.42 | ||
| Coefficient of Friction | ASTM D3702 | ||
| -- 2 | 0.27 | ASTM D3702 | |
| -- 3 | 0.29 | ASTM D3702 | |
| Wear Factor | ASTM D3702 | ||
| Drying: 4 m/s, 0.2 MPa (800 fpm, 31.25 psi) | 17.0 | in³·min^-10/ft·lb·hr | ASTM D3702 |
| Drying: 0.25 m/s, 3.4 MPa (50 fpm, 500 psi) | 21.0 | in³·min^-10/ft·lb·hr | ASTM D3702 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Coefficient of Linear Thermal Expansion | 1.4E-5 | cm/cm/°C | ASTM D696 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 43 | J/m | ASTM D256 |
| Unnotched Izod Impact | 220 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 278 | °C | ASTM D648 |
| Thermal Conductivity | 0.81 | W/m/K | ASTM C177 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 6.0E+6 | ohms | ASTM D257 |
| Volume Resistivity | 2.0E+7 | ohms·cm | ASTM D257 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 177 | °C | |
| Drying Time | 3.0 | hr | |
| Suggested Max Moisture | 0.050 | % | |
| Rear Temperature | 304 | °C | |
| Nozzle Temperature | 371 | °C | |
| Mold Temperature | 199 - 216 | °C | |
| Back Pressure | 6.89 | MPa | |
| Screw Speed | 50 - 100 | rpm | |
| Screw L/D Ratio | 18.0:1.0 - 24.0:1.0 |
| Injection instructions |
|---|
| 最低干燥条件：350 °F 温度下3小时， 300 °F 温度下4小时， 或250 °F 温度下16小时。 压缩比：1：1或1.5：1 开始时，压力保持在6,000-8,000 psi ，几秒钟后，降至～3,000-5,000psi（ 20.69-34.48MPa） ，进行保压。 成型部件需进行后固化。 |
| Note Message | |
|---|---|
| 1 . | Previously, ASTM standard test method D1708 was used to measure the tensile properties of PAI and similar materials because small samples can save more materials. The most widely used now is the ASTM D638 1 Bar specimen. The D1708 value contained is only used as a historical reference and is not used for comparison with the D638 value. |
| 2 . | Drying: 4 m/s, 0.2 MPa (800 fpm, 31.25 psi) |
| 3 . | Drying: 0.25 m/s, 3.4 MPa (50 fpm, 500 psi) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TPV Elastoprene® N40D-i | ELASTORSA Elastomeros Riojanos S.A. | PP+EPDM | TPV Elastoprene® |
| Elastron® G P.G401.A45.B | Elastron USA, Inc. | SEBS | Elastron® G |
| Kumho ABS H2938 | Korea Kumho Petrochemical Co., Ltd. | ABS | Kumho ABS |
| Hyundai EP Adhesives LE130A/1002 | HYUNDAI EP Co., Ltd. | PE, Unspecified | Hyundai EP Adhesives |
| Lupox® TE5011 | LG Chem Ltd. | PC+PBT | Lupox® |