Akulon® K224-G3-FC NA99001
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | DSM Engineering Plastics |
| Trademark: | Akulon® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 0SHBQB_Akulon-K224-G3-FC-NA99001.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Akulon® K224-G3-FC NA99001 is a Polyamide 6 (Nylon 6) material filled with 15% glass fiber. It is available in Europe. Important attributes of Akulon® K224-G3-FC NA99001 are:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.23 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | |||
| Across Flow | 0.96 | -- | % | |
| Flow | 0.32 | -- | % | |
| Water Absorption | ISO 62 | |||
| Saturation, 23°C | 7.6 | -- | % | |
| Equilibrium, 23°C, 50% RH | 2.3 | -- | % |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 6000 | 3500 | MPa | ISO 527-2 |
| Tensile Stress (Break) | 125 | 70.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 3.0 | 12 | % | ISO 527-2 |
| Flexural Modulus | 5200 | -- | MPa | ISO 178 |
| Flexural Stress | 170 | -- | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -30°C | 6.0 | 6.0 | kJ/m² | |
| 23°C | 7.0 | 15 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
| -30°C | 40 | 40 | kJ/m² | |
| 23°C | 45 | 80 | kJ/m² |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, Unannealed | 215 | -- | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 195 | -- | °C | ISO 75-2/A |
| Melting Temperature 1 | 220 | -- | °C | ISO 11357-3 |
| CLTE | ISO 11359-2 | |||
| Flow | 3.0E-5 | -- | cm/cm/°C | |
| Transverse | 8.0E-5 | -- | cm/cm/°C |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | -- | 1.0E+14 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+15 | 1.0E+15 | ohms·cm | IEC 60093 |
| Electric Strength | 35 | 25 | kV/mm | IEC 60243-1 |
| Relative Permittivity | IEC 60250 | |||
| 100 Hz | 3.50 | 14.0 | ||
| 1 MHz | 4.70 | 1.50 | ||
| Dissipation Factor | IEC 60250 | |||
| 100 Hz | 5.5E-3 | 0.15 | ||
| 1 MHz | 0.018 | 0.12 | ||
| Comparative Tracking Index | -- | 600 | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flammability Classification | IEC 60695-11-10, -20 | |||
| 0.750 mm | HB | -- | ||
| 1.50 mm | HB | -- |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 4.0 to 8.0 | hr | |
| Rear Temperature | 255 to 265 | °C | |
| Middle Temperature | 265 to 275 | °C | |
| Front Temperature | 265 to 280 | °C | |
| Nozzle Temperature | 260 to 280 | °C | |
| Processing (Melt) Temp | 250 to 285 | °C | |
| Mold Temperature | 50.0 to 80.0 | °C | |
| Injection Rate | Moderate-Fast | ||
| Back Pressure | 3.00 to 10.0 | MPa | |
| Screw Compression Ratio | 2.5:1.0 |
| Note Message | |
|---|---|
| 1 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 208 A RC HS Black | RTP Company | Nylon 6 | RTP |
| SCHULAFORM® 9 A GF 20 | A. Schulman Europe | Acetal (POM) Copolymer | SCHULAFORM® |
| Xuchuan XCW-8845C | Xuchuan Chemical (Suzhou) Co., Ltd | PUR, Unspecified | Xuchuan |
| Karina WHITE PVC COMPOUND 752D10/151-B-IS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Plaslube® PC / ABS 1950 | Techmer Engineered Solutions | PC+ABS | Plaslube® |