TOTAL Polypropylene PPH 7060
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | TOTAL Refining & Chemicals |
| Trademark: | TOTAL Polypropylene |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 0RnRBn_TOTAL-Polypropylene-PPH-7060.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Polypropylene PPH 7060 is a homopolymer with a medium molecular weight distribution and a Melt Flow Index of 12 g/10 min for the cast extrusion of films with excellent optical properties and high stiffness. Polypropylene PPH 7060 is intended for the injection moulding of packaging containers, toys, domestic appliances, garden furniture and caps & closures. Polypropylene PPH 7060 is intended for applications like sensitive food packaging, labeling. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.905 | g/cm³ | ISO 1183 |
| Apparent Density | 0.53 | g/cm³ | ISO 60 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 12 | g/10 min | ISO 1133 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 95 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 1550 | MPa | ISO 527-2 |
| Tensile Stress (Yield) | 32.0 | MPa | ISO 527-2 |
| Tensile Strain (Yield) | 10 | % | ISO 527-2 |
| Flexural Modulus | 1450 | MPa | ISO 178 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 50 | µm | |
| Tensile Stress | ISO 527-3 | ||
| MD : Yield, 50 µm, Cast Film | 23.0 | MPa | |
| TD : Yield, 50 µm, Cast Film | 23.0 | MPa | |
| MD : Break, 50 µm, Cast Film | 44.0 | MPa | |
| TD : Break, 50 µm, Cast Film | 34.0 | MPa | |
| Tensile Elongation | ISO 527-3 | ||
| MD : Break, 50 µm, Cast Film | 500 | % | |
| TD : Break, 50 µm, Cast Film | 600 | % | |
| Dart Drop Impact (50 µm, Cast Film) | 270 | g | ISO 7765-1 |
| Elmendorf Tear Strength 1 | ISO 6383-2 | ||
| MD : 50.0 µm | 10.0 | kN/m | |
| TD : 50.0 µm | 28.0 | kN/m |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 4.5 | kJ/m² | ISO 179 |
| Notched Izod Impact Strength (23°C) | 3.5 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 100 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 55.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | |||
| -- | 152 | °C | ISO 306/A50 |
| -- | 87.0 | °C | ISO 306/B50 |
| Melting Temperature (DSC) | 165 | °C | ISO 3146 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°, 50.0 µm, Cast Film) | 85 | ASTM D2457 | |
| Haze (50.0 µm, Cast Film) | 4.0 | % | ISO 14782 |
| Note Message | |
|---|---|
| 1 . | Cast Film |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Makroblend® KU2-7912 | Covestro - Polycarbonates | PC+PBT | Makroblend® |
| Aaroprene® ATPO 3000 80A | Aaron Industries Corp. | TPO (POE) | Aaroprene® |
| Celanex® 3300-2 | Celanese Corporation | PBT | Celanex® |
| DENILEN M 3015 | Vamp Tech | PP, Unspecified | DENILEN |
| POLYfill PPH GF8030 PD1 VT2 | Polykemi AB | PP Homopolymer | POLYfill |