Adflex Z108SE
| Category: | Polyolefin, Unspecified , Polyolefin |
| Manufacturer: | LyondellBasell Industries |
| Trademark: | Adflex |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 0RgGxk_Adflex-Z108SE.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Adflex Z 108 SE is a reactor TPO (thermoplastic polyolefin) manufactured using the LyondellBasell's proprietary Catalloy process technology. Adflex Z 108 SE features a very high softness, a very low flexural modulus and a high melt flow rate. It is used for injection molding, impact modification, extrusion coating, soft compounding, film and fiber applications. It is also ideal for the modification of polypropylene homopolymer and random copolymer without altering the transparency. The grade is available in natural pellet form. For regulatory compliance information see Adflex Z 108 SE Product Stewardship Bulletin (PSB). |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 27 | g/10 min | ISO 1133 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness | |||
| Shore D | 36 | ASTM D2240 | |
| Shore D, 15 sec | 36 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ISO 527-2 | ||
| Yield | 7.80 | MPa | |
| Break | 15.8 | MPa | |
| Tensile Strain | ISO 527-2 | ||
| Yield | 28 | % | |
| Break | 1100 | % | |
| Flexural Modulus | 170 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | ||
| -40°C | 2.0 | kJ/m² | |
| -20°C | 13 | kJ/m² | |
| 23°C | 59 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (0.45 MPa, Unannealed) | 42.8 | °C | ISO 75-2/B |
| Vicat Softening Temperature | 72.8 | °C | ISO 306/A50 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| COPEC® CC8OCN (Series: VS/AD1) | KRAIBURG TPE | TPE | COPEC® |
| Hiprolon® 200 VN LM | Arkema | Nylon 1010 | Hiprolon® |
| Lion Idemitsu Composites PPS C-140SC | Lion Idemitsu Composites Co., Ltd. | PPS | Lion Idemitsu Composites PPS |
| Karina CRISTAL CLEAR PVC COMPOUND 83/206-IS-SI | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Moplen PM784W-H | LyondellBasell Industries | PP Impact Copolymer | Moplen |