KPOL-PP K-PPH 8.5F

Category:	PP Homopolymer , Polypropylene Homopolymer
Manufacturer:	KPOL Chem Co.
Trademark:	KPOL-PP
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	0RWxtQ_KPOL-PP-K-PPH-8-5F.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

WECHAT

Message

Polypropylene Homopolymer Film

Applications

The KPOL® K-PPH 8.5F is a medium melt flow rate homopolymer, with slip and antiblocking agents.

It is suitable for blown film extrusion. This product features good impact strenght, excellent gloss and transparency, good slipping and good weldability.

Characteristics

Blown Film Extrusion. Films made with K-PPH 8.5F show very high transparency, high gloss, good printability after corona treatment and good sealability.

Coil for automatic, general purpose, food and textile packaging.

General Information
Additive	Antiblock Antioxidant Slip
Features	Antiblocking Antioxidant Excellent Printability Food Contact Acceptable Good Impact Resistance High Gloss Homopolymer Medium Flow Slip Weldable
Uses	Film Food Packaging Packaging
Agency Ratings	FDA 21 CFR 177.1520
Appearance	Clear/Transparent
Forms	Pellets
Processing Method	Blown Film Film Extrusion

Physical	Nominal Value	Unit	Test Method
Density	0.905	g/cm³	ASTM D1505
Melt Mass-Flow Rate (MFR) (230°C/2.16 kg)	8.5	g/10 min	ASTM D1238

Mechanical	Nominal Value	Unit	Test Method
Tensile Strength ¹(Yield, Compression Molded)	35.0	MPa	ASTM D638
Tensile Elongation ²(Break, Compression Molded)	11	%	ASTM D638
Flexural Modulus - 1% Secant (Compression Molded)	1400	MPa	ASTM D790

Films	Nominal Value	Unit	Test Method
Dart Drop Impact ³	300	g	ASTM D1709

Impact	Nominal Value	Unit	Test Method
Notched Izod Impact (Compression Molded)	35	J/m	ASTM D256

Thermal	Nominal Value	Unit	Test Method
Vicat Softening Temperature	150	°C	ASTM D1525 ⁴

Optical	Nominal Value	Unit	Test Method
Gardner Gloss (20°, 50.0 µm, Blown Film)	100		ASTM D523
Haze (50.0 µm, Blown Film)	2.8	%	ASTM D1003

Note Message
1 .	Type IV, 50 mm/min
2 .	Type IV, 50 mm/min
3 .	F50
4 .	Rate A (50°C/h), Loading 1 (10 N)

Resin Grade	Manufacturer	Category	Trademark
TAIRIPRO K8802	Formosa Plastics Corporation	PP Impact Copolymer	TAIRIPRO
Boltaron 3045 TruPrint	Boltaron Performance Products	PVC, Rigid	Boltaron
Hanwha Total PP BI1000	HANWHA TOTAL PETROCHEMICALS Co., Ltd.	PP, Unspecified	Hanwha Total PP
HiFill® PP GF20 CC LE	Techmer Engineered Solutions	PP, Unspecified	HiFill®
Infino GW-3330	LOTTE ADVANCED MATERIALS CO., LTD.	PC	Infino