Stat-Tech™ AS-1000 AS Black
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | PolyOne Corporation |
| Trademark: | Stat-Tech™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 0RIUUH_Stat-Tech-AS-1000-AS-Black.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Stat-Tech™ Electrically Conductive Compounds are specifically engineered to provide anti-static, ESD and RFI/EMI shielding performance for critical electronic equipment applications. These compounds combine the performance of select engineering resins with reinforcing additives such as carbon powder, carbon fiber, nickel-coated carbon fiber and stainless steel fiber, for low to high levels of conductivity depending upon application requirements. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.09 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | 0.10 to 0.90 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1 | 1300 | MPa | ASTM D638 |
| Tensile Strength (Yield) | 36.0 | MPa | ASTM D638 |
| Tensile Elongation 2(Break) | 12 | % | ASTM D638 |
| Flexural Modulus | 1590 | MPa | ASTM D790 |
| Flexural Strength | 50.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.18 mm, Injection Molded) | 140 | J/m | ASTM D256A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed, 6.35 mm | 82.0 | °C | |
| 1.8 MPa, Unannealed, 6.35 mm | 69.0 | °C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+9 to 1.0E+11 | ohms | ASTM D257 |
| Volume Resistivity | 1.0E+9 to 1.0E+11 | ohms·cm | ASTM D257 |
| Static Decay | |||
| (Mil-B-81705C), 12% RH, 5000 kV to 50 kV | 0.3 | sec | |
| (Mil-B-81705C), 50% RH, 5000 kV to 50 kV | 0.1 | sec |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Processing (Melt) Temp | 227 to 238 | °C |
| Note Message | |
|---|---|
| 1 . | Type I, 5.1 mm/min |
| 2 . | Type I, 5.1 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| ASTALAC™ ABS KMS | Marplex Australia Pty. Ltd. | ABS | ASTALAC™ |
| Cellophane™ 320MS | Innovia Films Ltd. | Cellulose, Regenerated | Cellophane™ |
| Estane® 58226 TPU | Lubrizol Advanced Materials, Inc. | TPU-Polyester | Estane® |
| Globalprene® 1484F | Lee Chang Yung Chemical Industry Corp. | SBS | Globalprene® |
| NORYL™ NH7111E resin | SABIC Innovative Plastics | PPE+PS | NORYL™ |