Romiloy® 6040 E UV
| Category: | ASA+PC , Acrylonitrile Styrene Acrylate + PC |
| Manufacturer: | ROMIRA GmbH |
| Trademark: | Romiloy® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 0Q3ibA_Romiloy-6040-E-UV.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Romiloy®6040 E UV is an acrylonitrile-styrene-acrylate PC (ASA PC) material,. This product is available in Europe and is processed by extrusion or injection molding. Romiloy®The main characteristics of 6040 E UV are:
|
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.14 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) | ISO 1133 | ||
| 220°C/10.0 kg | 6.0 | g/10 min | ISO 1133 |
| 260°C/5.0 kg | 14 | g/10 min | ISO 1133 |
| Molding Shrinkage (23°C) | 0.40 - 0.70 | % | ISO 294-4 |
| Water Absorption (23°C, 24 hr) | 0.30 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 2600 | MPa | ISO 527-2/1 |
| Tensile Stress (Yield, 23°C) | 60.0 | MPa | ISO 527-2/50 |
| Tensile Strain (Break, 23°C) | 100 | % | ISO 527-2/50 |
| Flexural Modulus 1(23°C) | 2500 | MPa | ISO 178 |
| Flexural Stress 2(23°C) | 95.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30°C | 20 | kJ/m² | ISO 179/1eA |
| 23°C | 55 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -30°C | No Break | ISO 179/1eU | |
| 23°C | No Break | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 123 | °C | ISO 306/B50 |
| CLTE - Flow (23 to 55°C) | 8.5E-5 | cm/cm/°C | ISO 11359-2 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.50 mm) | HB | UL 94 |
| Additional Information |
|---|
| The value listed as Molding Shrinkage ISO 294-4, was tested in accordance with DIN 16901.The value listed as Coefficient of Linear Thermal Expansion ISO 11359-1-2, was tested in accordance with DIN 53752. |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 60.0 - 100 | °C | |
| Drying Time | 2.0 - 4.0 | hr | |
| Suggested Max Moisture | 0.050 | % | |
| Suggested Max Regrind | 5 | % | |
| Processing (Melt) Temp | 240 - 260 | °C | |
| Mold Temperature | 60.0 - 100 | °C | |
| Injection Rate | Moderate |
| Injection instructions |
|---|
| Back Pressure: <20%Holding Pressure: Low |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 60.0 - 100 | °C | |
| Drying Time | 2.0 - 4.0 | hr | |
| Suggested Max Moisture | < 0.050 | % | |
| Cylinder Zone 1 Temp. | 210 - 250 | °C | |
| Cylinder Zone 2 Temp. | 210 - 250 | °C | |
| Cylinder Zone 3 Temp. | 210 - 250 | °C | |
| Cylinder Zone 4 Temp. | 210 - 250 | °C | |
| Cylinder Zone 5 Temp. | 210 - 250 | °C | |
| Melt Temperature | < 260 | °C |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TES J-50/40 BK223 | Techmer Engineered Solutions | PC | TES |
| Verolloy DR210 | PlastxWorld Inc. | PC+SMA | Verolloy |
| Later 4-V0 | LATI S.p.A. | PBT | Later |
| Hostacom BB 1162 F M C13034 | LyondellBasell Industries | PP Copolymer | Hostacom |
| LNP™ THERMOCOMP™ EC006 compound | SABIC Innovative Plastics | PEI | LNP™ THERMOCOMP™ |