DIAMALOY ABSPC 750 HF is a Polycarbonate + ABS (PC+ABS) product. It is available in North America. Characteristics include:
|
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Agency Ratings |
|
| UL File Number |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.18 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) 1 | |||
| 200°C/5.0 kg | 26 | g/10 min | ASTM D1238 |
| 230°C/3.8 kg | 27 | g/10 min | ASTM D1238 |
| 230°C/3.8 kg | 14 | g/10 min | ISO 1133 |
| Melt Volume-Flow Rate (MVR) (230°C/3.8 kg) | 14.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage - Flow | 0.40 to 0.80 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2700 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield 2 | 60.0 | MPa | ASTM D638 |
| Yield | 55.0 | MPa | ISO 527-2/50 |
| Tensile Elongation | |||
| Yield 3 | 2.5 | % | ASTM D638 |
| Break, Injection Molded 4 | > 100 | % | ISO 527-2/50 |
| Flexural Modulus | |||
| -- 5 | 2650 | MPa | ASTM D790B |
| -- 6 | 2840 | MPa | ISO 178 |
| Flexural Stress 7 | 89.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 17 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact | |||
| 3.18 mm | 530 | J/m | ASTM D256A |
| 23°C | 42 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 1.8 MPa, Unannealed, 3.18 mm | 82.2 | °C | ASTM D648 |
| 1.8 MPa, Unannealed | 73.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 105 | °C | ASTM D1525 8 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.50 mm | V-0 | ||
| 2.00 mm | V-0 5VB | ||
| 3.00 mm | V-0 5VB |
| Note Message | |
|---|---|
| 1 . | Procedure A |
| 2 . | Type I, 51 mm/min |
| 3 . | Type I, 51 mm/min |
| 4 . | 1.95 in/min |
| 5 . | Method I (3 point load), 1.3 mm/min |
| 6 . | 2.0 mm/min |
| 7 . | 2.0 mm/min |
| 8 . | Rate B (120°C/h), Loading 1 (10 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| POLYMAN® (ABS) LC 165 | A. Schulman Europe | ABS | POLYMAN® |
| RAMSTER PE321G6 | Polyram Ram-On Industries | PET | RAMSTER |
| TABOREX TA 2150 HD | SILON s.ro | TP, Unspecified | TABOREX |
| Fainplast PVC RH 210/K1 | Fainplast Compounds S.r.l | PVC, Rigid | Fainplast PVC |
| KOPLA PA6 KRE1010 | KOPLA Co., Ltd. | Nylon 6+ABS | KOPLA PA6 |