LNP™ STAT-KON™ DEL22P compound
| Category: | PC , Polycarbonate |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ STAT-KON™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 0PgovP_LNPSTATKONDEL22Pcompound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP STAT-KON* DEL22P is a compound based on Polycarbonate resin containing PTFE, Carbon Fiber. Added features of this material include: Electrically Conductive. Also known as: LNP* STAT-KON* Compound DCL-4022 EP Product reorder name: DEL22P |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.30 | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage | Internal method | ||
| Flow | 0.10 - 0.30 | % | Internal method |
| Transverse flow 1 | 0.40 - 0.60 | % | Internal method |
| Water Absorption | |||
| 24 hr, 50% RH | 0.10 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 0.18 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 2 | 7900 | MPa | ASTM D638 |
| -- | 8170 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Fracture | 100 | MPa | ASTM D638 |
| Fracture | 101 | MPa | ISO 527-2 |
| Tensile Elongation (Break) | 2.0 | % | ASTM D638, ISO 527-2 |
| Flexural Modulus | |||
| -- | 5690 | MPa | ASTM D790 |
| -- | 152 | MPa | ISO 178 |
| Flexural Strength | 152 | MPa | ASTM D790 |
| Coefficient of Friction | ASTM D3702 Modified | ||
| With self-dynamics | 0.55 | ASTM D3702 Modified | |
| With Self-Static | 0.52 | ASTM D3702 Modified | |
| Wear Factor - Washer | 15.0 | 10^-10 in^5-min/ft-lb-hr | ASTM D3702 Modified |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 75 | J/m | ASTM D256 |
| 23°C 3 | 6.3 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 280 | J/m | ASTM D4812 |
| 23°C 4 | 34 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Energy at Peak Load | 13.0 | J | ASTM D3763 |
| -- | 102 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 1.8 MPa, unannealed, 3.20mm | 134 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 64.0mm span 5 | 143 | °C | ISO 75-2/Af |
| Linear thermal expansion coefficient | |||
| Flow : -40 to 40°C | 1.4E-5 | cm/cm/°C | ASTM E831 |
| Flow : -40 to 40°C | 1.5E-5 | cm/cm/°C | ISO 11359-2 |
| Lateral : -40 to 40°C | 7.6E-5 | cm/cm/°C | ASTM E831, ISO 11359-2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+2 - 1.0E+6 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+2 | ohms·cm | IEC 60093 |
| Note Message | |
|---|---|
| 1 . | 0.75 to 2.3 mm |
| 2 . | 50 mm/min |
| 3 . | 80*10*4 |
| 4 . | 80*10*4 |
| 5 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Monprene® CP-13235 | Teknor Apex Company | TPE | Monprene® |
| Tarnamid® T- 27 GF30 FRV0 | Grupa Azoty S.A. | Nylon 6 | Tarnamid® |
| Vistek 1862 U | Visual Polymer Technologies, LLC | TP, Unspecified | Vistek |
| Nanjing Hongrui PA66 A326 | Nanjing Hongrui Engineering Plastics Co., Ltd. | Nylon 66 | Nanjing Hongrui PA66 |
| Bayblend® FR3010 HF | Covestro - Polycarbonates | PC+ABS | Bayblend® |