LNP™ THERMOCOMP™ EF006H compound
| Category: | PEI , Polyether Imide |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ THERMOCOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 0PbR7M_LNPTHERMOCOMPEF006Hcompound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP THERMOCOMP EF006H is a compound based on Polyetherimide resin containing Glass Fiber. Also known as: LNP* THERMOCOMP* Compound EF-1006 EES Product reorder name: EF006H |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.52 | g/cm³ | ASTM D792 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1 | 10300 | MPa | ASTM D638 |
| Tensile Strength (Break) | 167 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 2.3 | % | ASTM D638 |
| Flexural Modulus | 10300 | MPa | ASTM D790 |
| Flexural Strength | 262 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 85 | J/m | ASTM D256 |
| Unnotched Izod Impact (23°C) | 640 | J/m | ASTM D4812 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 3.20 mm) | 204 | °C | ASTM D648 |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RABALON® FJ5371C | Mitsubishi Chemical Performance Polymers, Inc. | TPE | RABALON® |
| SCHULAMID® 66 GF 30 HR | A. Schulman Europe | Nylon 66 | SCHULAMID® |
| Wellamid® NY1599-N | Wellman Engineering Resins | Nylon 66 | Wellamid® |
| NaturePlast NP DU 103 | NaturePlast | Nylon 1012 | NaturePlast |
| LCA® PC-143 Clear | UniPlas, Inc. | PC | LCA® |