ULTEM™ 4211 resin
| Category: | PEI , Polyether Imide |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | ULTEM™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 0Paaiu_ULTEM-4211-resin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 20% Glass fiber filled and PTFE filled, standard flow Polyetherimide (Tg 217C). ECO Conforming. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Agency Ratings |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.48 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (337°C/6.6 kg) | 10 | g/10 min | ASTM D1238 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Yield) | 129 | MPa | ASTM D638 |
| Tensile Elongation 2(Break) | 3.0 | % | ASTM D638 |
| Flexural Modulus 3(100 mm Span) | 7100 | MPa | ASTM D790 |
| Flexural Strength 4(Break, 100 mm Span) | 193 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Reverse Notch Izod Impact (3.20 mm) | 440 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 6.40 mm) | 212 | °C | ASTM D648 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 135 | °C | |
| Drying Time | 4.0 to 6.0 | hr | |
| Drying Time, Maximum | 10 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Suggested Shot Size | 40 to 60 | % | |
| Rear Temperature | 338 to 360 | °C | |
| Middle Temperature | 343 to 366 | °C | |
| Front Temperature | 349 to 371 | °C | |
| Nozzle Temperature | 349 to 371 | °C | |
| Processing (Melt) Temp | 349 to 371 | °C | |
| Mold Temperature | 135 to 163 | °C | |
| Back Pressure | 0.345 to 0.689 | MPa | |
| Screw Speed | 40 to 70 | rpm | |
| Vent Depth | 0.025 to 0.076 | mm |
| Note Message | |
|---|---|
| 1 . | Type I, 5.0 mm/min |
| 2 . | Type I, 5.0 mm/min |
| 3 . | 2.6 mm/min |
| 4 . | 2.6 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 1407 Z | RTP Company | PESU | RTP |
| Taitacell EPS 361S | Taita Chemical Company, Ltd. | PS (EPS) | Taitacell |
| UmaPET ULM | Ester Industries Ltd. | PET | UmaPET |
| Softell TKG 300N C12453 | LyondellBasell Industries | PP Copolymer | Softell |
| LEXAN™ 923 resin | SABIC Innovative Plastics | PC | LEXAN™ |