LNP™ THERMOCOMP™ JF006LXZ compound
| Category: | PESU , Polyethersulfone |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ THERMOCOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 0P1P51_LNP-THERMOCOMP-JF006LXZ-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP THERMOCOMP JF006LXZ is a compound based on Polyethersulfone resin containing 30% Glass Fiber. Added features of this material include: Low Extractible. Also known as: LNP* THERMOCOMP* Compound JF-1006 LE Product reorder name: JF006LXZ |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.61 | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage | |||
| Flow : 24 hr | 0.20 | % | ASTM D955 |
| Across Flow : 24 hr | 0.70 | % | ASTM D955 |
| Across Flow : 24 hr | 0.69 | % | ISO 294-4 |
| Flow : 24 hr | 0.25 | % | ISO 294-4 |
| Water Absorption (24 hr, 50% RH) | 0.30 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 9790 | MPa | ASTM D638 |
| -- | 10200 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Break | 113 | MPa | ASTM D638 |
| Break | 99.0 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Break | 1.8 | % | ASTM D638 |
| Break | 1.4 | % | ISO 527-2 |
| Flexural Modulus | 9240 | MPa | ASTM D790, ISO 178 |
| Flexural Strength | |||
| -- | 172 | MPa | ASTM D790 |
| -- | 222 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 59 | J/m | ASTM D256 |
| 23°C 2 | 6.8 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 430 | J/m | ASTM D4812 |
| 23°C 3 | 30 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Energy at Peak Load | 13.0 | J | ASTM D3763 |
| -- | 3.00 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed, 3.20 mm | 218 | °C | |
| 1.8 MPa, Unannealed, 3.20 mm | 212 | °C | |
| CLTE | |||
| Flow : -40 to 40°C | 3.1E-5 | cm/cm/°C | ASTM E831 |
| Flow : -40 to 40°C | 3.0E-5 | cm/cm/°C | ISO 11359-2 |
| Transverse : -40 to 40°C | 3.6E-5 | cm/cm/°C | ASTM E831, ISO 11359-2 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 to 149 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.050 | % | |
| Rear Temperature | 343 to 354 | °C | |
| Middle Temperature | 360 to 371 | °C | |
| Front Temperature | 371 to 382 | °C | |
| Processing (Melt) Temp | 354 to 371 | °C | |
| Mold Temperature | 138 to 149 | °C | |
| Back Pressure | 0.344 to 0.689 | MPa | |
| Screw Speed | 60 to 100 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SLOVALEN® PH 49 GF 50 | Plastcom | PP, Unspecified | SLOVALEN® |
| ABS Proquigel AM-F | Proquigel | ABS | ABS Proquigel |
| ELASTOSIL® E 303 | Wacker Chemie AG | Silicone | ELASTOSIL® E |
| Hangzhou Keli ACS C-130 | Hangzhou Keli Chemical Co., Ltd. | ACS | Hangzhou Keli ACS |
| Sylvin 9812-65 Red 6311 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |