LNP™ THERMOCOMP™ YF003S compound
| Category: | TPEE , Thermoplastic Polyester Elastomer |
| Manufacturer: | SABIC Innovative Plastics Europe |
| Trademark: | LNP™ THERMOCOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 0OIKOE_LNP-THERMOCOMP-YF003S-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP THERMOCOMP YF003S is a compound based on Polyester Elastomer containing Glass Fiber. Added features include; Heat Stabilized. Also known as: LNP* THERMOCOMP* Compound YF-1003 HS NAT Product reorder name: YF003S |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.30 | g/cm³ | ISO 1183 |
| Molding Shrinkage - Flow | 0.50 | % | Internal Method |
| Water Absorption (23°C, 24 hr) | 0.54 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 1500 | MPa | ISO 527-2/1 |
| Tensile Stress | ISO 527-2/50 | ||
| Yield | 43.0 | MPa | |
| Break | 42.0 | MPa | |
| Tensile Strain (Yield) | 15 | % | ISO 527-2/50 |
| Flexural Modulus 1 | 1200 | MPa | ISO 178 |
| Flexural Stress | 45.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength 2(23°C) | 28 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength 3(23°C) | 85 | kJ/m² | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 4 | |||
| 0.45 MPa, Unannealed, 64.0 mm Span | 163 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed, 64.0 mm Span | 121 | °C | ISO 75-2/Af |
| CLTE | ISO 11359-2 | ||
| Flow : 23 to 60°C | 3.4E-5 | cm/cm/°C | |
| Transverse : 23 to 60°C | 2.0E-4 | cm/cm/°C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.10 | % | |
| Rear Temperature | 182 to 193 | °C | |
| Middle Temperature | 204 to 216 | °C | |
| Front Temperature | 227 to 238 | °C | |
| Processing (Melt) Temp | 216 to 238 | °C | |
| Mold Temperature | 26.7 to 54.4 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 |
| 4 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sylvin RP 3504 White | Sylvin Technologies Incorporated | PVC, Rigid | Sylvin |
| Nanjing Hongrui PA66 A401 | Nanjing Hongrui Engineering Plastics Co., Ltd. | Nylon 66 | Nanjing Hongrui PA66 |
| NITRIFLEX NP-6121 | NITRIFLEX | NBR | NITRIFLEX |
| INEOS PP 101-GF02 | INEOS Olefins & Polymers Europe | PP Homopolymer | INEOS PP |
| LOXIM 315 01 HB | LOXIM Industries Private Limited | Nylon 6 | LOXIM |