Hiprolon® 200 FN
| Category: | Nylon 1010 , Polyamide 1010 |
| Manufacturer: | Arkema |
| Trademark: | Hiprolon® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 0MWXz1_Hiprolon-200-FN.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Hiprolon® 200 FN is a polyamide produced from a renewable source. This grade is a polyamide 10.10 neat resin. |
| General Information | |
|---|---|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.04 | g/cm³ | ISO 1183 |
| Water Absorption (Equilibrium, 23°C, 50% RH) | 0.80 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 1200 | MPa | ISO 527-2 |
| Tensile Stress (Yield) | 45.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | > 50 | % | ISO 527-2 |
| Flexural Modulus | 1200 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30°C | 7.0 | kJ/m² | |
| 23°C | 10 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -30°C | No Break | ||
| 23°C | No Break |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 50.0 | °C | ISO 75-2/A |
| Melting Temperature | 202 | °C | ISO 11357-3 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| ISO Shortname | PA 1010, 18-010 | ISO 1874 | |
| Renewable Carbon Conent | > 99 | % | ASTM D6866 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 to 90.0 | °C | |
| Drying Time | 4.0 | hr | |
| Processing (Melt) Temp | 220 to 280 | °C | |
| Mold Temperature | 20.0 to 60.0 | °C |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 to 90.0 | °C | |
| Drying Time | 4.0 | hr | |
| Melt Temperature | 210 to 260 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| PURFLEX™ TPO D80-BK09 | Pier One Polymers, Inc. | TPE | PURFLEX™ |
| MELOPAS® MF 150 | RASCHIG GmbH | Mel Formald | MELOPAS® |
| VITAMIDE® BY16 | A. Schulman Europe | Nylon 6 | VITAMIDE® |
| EXCELINK 3300B | JSR Corporation | TPV | EXCELINK |
| Tunhe PBT TH6075 | Xinjiang Blueridge Tunhe Chemical Industry Co.,Ltd | PBT | Tunhe PBT |