Keyflex® BT HB9255D
| Category: | TPC-ET , Thermoplastic Copolyester Elastomer |
| Manufacturer: | LG Chem Ltd. |
| Trademark: | Keyflex® BT |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 0ML9G8_Keyflex-BT-HB9255D.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Description Medium Modulus, Black Color Application Air duct, Hose & Tubing |
| General Information | |
|---|---|
| Uses |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.16 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 3.0 | g/10 min | ASTM D1238 |
| Water Absorption (23°C, 24 hr) | 0.60 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D, 23°C, Injection Molded) | 47 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Break, 23°C, 2.00 mm, Injection Molded) | 34.3 | MPa | ASTM D638 |
| Tensile Elongation 2(Break, 23°C, 2.00 mm, Injection Molded) | 1000 | % | ASTM D638 |
| Flexural Modulus 3(23°C, 6.40 mm, Injection Molded) | 196 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ASTM D256 | ||
| -40°C, 6.40 mm, Injection Molded | 150 | J/m | |
| 23°C, 6.40 mm, Injection Molded | No Break |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed, 6.40 mm, Injection Molded) | 70.0 | °C | ASTM D648 |
| Peak Melting Temperature | 220 | °C | ASTM D3418 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 to 90.0 | °C | |
| Drying Time | 3.0 to 4.0 | hr | |
| Suggested Max Moisture | < 0.010 | % | |
| Cylinder Zone 1 Temp. | 220 to 240 | °C | |
| Cylinder Zone 2 Temp. | 230 to 250 | °C | |
| Cylinder Zone 3 Temp. | 230 to 250 | °C | |
| Cylinder Zone 4 Temp. | 230 to 250 | °C | |
| Adapter Temperature | 230 to 250 | °C | |
| Melt Temperature | 220 to 250 | °C | |
| Die Temperature | 220 to 260 | °C |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| 3 . | 15 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Resinoid 2016P | Resinoid Engineering Corporation | Phenolic | Resinoid |
| Braskem PE FH 35 | Braskem | LLDPE | Braskem PE |
| Hanwha Total PP BI970 | HANWHA TOTAL PETROCHEMICALS Co., Ltd. | PP, High Crystal | Hanwha Total PP |
| HiFill® PBT FR-DE | Techmer Engineered Solutions | PBT | HiFill® |
| LNP™ STAT-LOY™ AF306 compound | SABIC Innovative Plastics Asia Pacific | ABS | LNP™ STAT-LOY™ |