Borealis PE FA7229
| Category: | LDPE , Low Density Polyethylene |
| Manufacturer: | Borealis AG |
| Trademark: | Borealis PE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 0MADlG_Borealis-PE-FA7229.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
FA7229 is a Low Density Polyethylene for Film Extrusion. Autoclave Technology. Includes Antioxidant and Cling additive. This grade is developed for production of blown cling film. FA7229 contains antioxidant and antifog/cling additives. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.922 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 4.0 | g/10 min | ISO 1133 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 40 | µm | |
| secant modulus | ASTM D882A | ||
| MD : 40 µm | 200 | MPa | ASTM D882A |
| TD : 40 µm | 180 | MPa | ASTM D882A |
| Tensile Strength | ISO 527-3 | ||
| MD : 40 µm | 24.0 | MPa | ISO 527-3 |
| TD : 40 µm | 18.0 | MPa | ISO 527-3 |
| Tensile Elongation | ISO 527-3 | ||
| MD : Break, 40 µm | 400 | % | ISO 527-3 |
| TD : Break, 40 µm | 650 | % | ISO 527-3 |
| Dart Drop Impact (40 µm) | 80 | g | ISO 7765-1 |
| Elmendorf Tear Strength | ISO 6383-2 | ||
| MD : 40 µm | 3.0 | N | ISO 6383-2 |
| TD : 40 µm | 2.0 | N | ISO 6383-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melting Temperature | 111 | °C | ISO 11357-3 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (40.0 µm) | 110 | ASTM D2457 | |
| Haze (40.0 µm) | 6.0 | % | ASTM D1003 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 140 - 180 | °C |
| Extrusion instructions |
|---|
| Draw Down: 15 to 20µThe web tension should not exceed 1,5% for a 25 micron or thinner film. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Flontech® FT-EK10-6 | Guarniflon S.p.A. - Flontech Division | PTFE | Flontech® |
| Karina PINK COLOR CONCENTRATE 39/ 63-FC-LMP | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| PENTAMID A GV15 H RC black | PENTAC Polymer GmbH | Nylon 66 | PENTAMID A |
| Sumiliteresin® PR-51820 | SBHPP | Phenolic | Sumiliteresin® |
| LNP™ THERMOCOMP™ DC006ER compound | SABIC Innovative Plastics | PC | LNP™ THERMOCOMP™ |