SLOVAMID® 66 GB 30 LS
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Plastcom |
| Trademark: | SLOVAMID® 66 |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 0LGcIF_SLOVAMID-66-GB-30-LS.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PA 66 injection for chemically reinforced glass beads 30%, light-stabilized, suitable for moldings with high strength and toughness, is used in the automotive, engineering and electrical industry. Use in environments where there is prolonged exposure to heat to 200°C. The decrease in tensile strength by 50% after 5000 hours at 170°C. Hobby tools, gears, housings electrical devices. Thermal stabilization of predetermined products in an environment with constant heat stress. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Processing Method |
|
| Resin ID (ISO 1043) |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.36 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (275°C/0.325 kg) | 3.0 | g/10 min | ISO 1133 |
| Molding Shrinkage | STM 64 0808 | ||
| Across Flow | 0.71 | % | |
| Flow | 0.63 | % | |
| Water Content | 0.15 | % | ISO 960 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 4700 | MPa | ISO 527-2 |
| Tensile Stress (Yield) | 85.0 | MPa | ISO 527-2 |
| Tensile Strain (Yield) | 8.0 | % | ISO 527-2 |
| Flexural Modulus | 4550 | MPa | ISO 178 |
| Flexural Stress | 180 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | ||
| -20°C | 8.0 | kJ/m² | |
| 23°C | 9.0 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179 | ||
| -20°C | 32 | kJ/m² | |
| 23°C | 36 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (0.45 MPa, Unannealed) | 250 | °C | ISO 75-2/B |
| Vicat Softening Temperature | 250 | °C | ISO 306/B |
| Melting Temperature (DSC) | 260 | °C | ISO 3146 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+14 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+17 | ohms·cm | IEC 60093 |
| Electric Strength | 40 | kV/mm | IEC 60243-1 |
| Comparative Tracking Index | 400 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | HB | UL 94 | |
| Glow Wire Ignition Temperature | 650 | °C | IEC 60695-2-13 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 4.0 | hr | |
| Processing (Melt) Temp | 280 to 300 | °C | |
| Mold Temperature | 60.0 to 90.0 | °C | |
| Injection Pressure | 70.0 to 120 | MPa |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Vipel® F085-ABB-00 | AOC, L.L.C. | Vinyl Ester | Vipel® |
| Axiall PVC 7840 | Axiall Corporation | PVC, Flexible | Axiall PVC |
| Gallonprene® GP410-5003 | Shenzhen Sungallon Rubber & Plastic Corporation Limited | TPE | Gallonprene® |
| Hylar® 5000 | Solvay Specialty Polymers | PVDF | Hylar® |
| ICORENE® 4014 | ICO Polymers EMEA, A Division of A. Schulman | PP Copolymer | ICORENE® |