Hostaform® S 27064 XAP² ™
| Category: | Acetal (POM) Copolymer , Acetal (POM) Copolymer |
| Manufacturer: | Celanese Corporation |
| Trademark: | Hostaform® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 0IPriQ_Hostaform-S-27064-XAP-.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Polyacetal copolymer, impact modified Easy flowing, elastomer-containing injection molding type based on HOSTAFORM C 27021 with high toughness and reduced emissions HB. Burning rate ISO 3795 and FMVSS 302 < 100 mm/min for more than 1 mm thickness. Emission according to VDA 275 < 5 mg/kg (natural colored grades) Ranges of applications: For thin-walled molded parts with high energy-absorbing capacity. Preliminary datasheet |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.37 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (190°C/2.16 kg) | 18.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage | ISO 294-4 | ||
| Vertical flow direction | 1.7 | % | ISO 294-4 |
| Flow direction | 1.8 | % | ISO 294-4 |
| Water Absorption (Saturation, 23°C) | 0.65 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 1700 | MPa | ISO 527-2/1A/1 |
| Tensile Stress (Yield) | 44.0 | MPa | ISO 527-2/1A/50 |
| Tensile Strain (Yield) | 10 | % | ISO 527-2/1A/50 |
| Nominal Tensile Strain at Break | 35 | % | ISO 527-2/1A/50 |
| Tensile Creep Modulus | ISO 899-1 | ||
| 1 hr | 1400 | MPa | ISO 899-1 |
| 1000 hr | 800 | MPa | ISO 899-1 |
| Flexural Modulus (23°C) | 1700 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30°C | 6.0 | kJ/m² | ISO 179/1eA |
| 23°C | 11 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -30°C | 110 | kJ/m² | ISO 179/1eU |
| 23°C, local fracture | 150 | kJ/m² | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 77.0 | °C | ISO 75-2/A |
| Melting Temperature 1 | 166 | °C | ISO 11357-3 |
| CLTE - Flow | 1.3E-4 | cm/cm/°C | ISO 11359-2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+13 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+13 | ohms·cm | IEC 60093 |
| Dielectric Strength | 28 | kV/mm | IEC 60243-1 |
| Relative Permittivity | IEC 60250 | ||
| 100 Hz | 4.40 | IEC 60250 | |
| 1 MHz | 4.40 | IEC 60250 | |
| Dissipation Factor | IEC 60250 | ||
| 100 Hz | 0.010 | IEC 60250 | |
| 1 MHz | 0.020 | IEC 60250 | |
| Comparative Tracking Index | 600 | V | IEC 60112 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 100 - 120 | °C | |
| Drying Time | 3.0 - 4.0 | hr | |
| Suggested Max Moisture | 0.15 | % | |
| Hopper Temperature | 20.0 - 30.0 | °C | |
| Rear Temperature | 170 - 180 | °C | |
| Middle Temperature | 180 - 190 | °C | |
| Front Temperature | 190 - 200 | °C | |
| Nozzle Temperature | 190 - 200 | °C | |
| Processing (Melt) Temp | 190 - 200 | °C | |
| Mold Temperature | 60.0 - 70.0 | °C | |
| Injection Pressure | 60.0 - 120 | MPa | |
| Injection Rate | Slow-Moderate | ||
| Holding Pressure | 60.0 - 120 | MPa | |
| Back Pressure | 0.00 - 2.00 | MPa |
| Injection instructions |
|---|
| Manifold Temperature: 190 to 200°CZone 4 Temperature: 190 to 200°CFeed Temperature: 60 to 80°C |
| Note Message | |
|---|---|
| 1 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Melos™ FM 1639 | Melos GmbH | TPO (POE) | Melos™ |
| Moplen HP500M | Shazand (Arak) Petrochemical Corporation | PP Homopolymer | Moplen |
| VECTOR® 4411A | Dexco Polymers LP | SIS | VECTOR® |
| Crastin® SK602 BK851 | DuPont Performance Polymers | PBT | Crastin® |
| Sylvin 83046-65 Natural | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |