AKROMID® A3 1 S1 black (3616)
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | AKRO-PLASTIC GmbH |
| Trademark: | AKROMID® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 0HY63l_AKROMID-A3-1-S1-black-3616-.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
AKROMID® A3 1 S1 black (3616) is a unreinforced, heat stabilised, cold impact strength polyamide 6.6. Applications are connecting and fixing systems in the automotive and elctro industry |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Resin ID (ISO 1043) |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density (23°C) | 1.10 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | |||
| Across Flow | 1.9 | -- | % | |
| Flow | 1.2 | -- | % | |
| Humidity Absorption - 62% RH (70°C) | 2.3 | -- | % | ISO 1110 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flexural Strain at Break 1 | 7.0 | -- | % | ISO 178 |
| Hardness | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Ball Indentation Hardness (H 358/30) | 111 | -- | MPa | ISO 2039-1 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 3000 | 2000 | MPa | ISO 527-2/1 |
| Tensile Stress (Yield) | 77.0 | 56.0 | MPa | ISO 527-2/50 |
| Tensile Strain | ISO 527-2/50 | |||
| Yield | 5.0 | 21 | % | |
| Break | > 20 | > 50 | % | |
| Flexural Modulus 2 | 2600 | -- | MPa | ISO 178 |
| Flexural Stress 3 | 100 | -- | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -30°C | 7.0 | -- | kJ/m² | |
| 23°C | 8.0 | -- | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
| -30°C | No Break | -- | ||
| 23°C | No Break | -- |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, Unannealed | 215 | -- | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 70.0 | -- | °C | ISO 75-2/A |
| Melting Temperature 4 | 262 | -- | °C | DIN EN 11357-1 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Volume Resistivity | 1.0E+15 | -- | ohms·cm | IEC 60093 |
| Comparative Tracking Index (Solution A) | 600 | -- | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating (1.60 mm) | HB | -- | UL 94 |
| Note Message | |
|---|---|
| 1 . | 2 mm/min |
| 2 . | 2.0 mm/min |
| 3 . | 2.0 mm/min |
| 4 . | 10 K/min, DSC |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Monprene® CP-49146 | Teknor Apex Company | TPE | Monprene® |
| Elastron® G G500.A30.B.PA | Elastron USA, Inc. | SEBS | Elastron® G |
| Huafon JF-P-8075 / JF-I-9818 | Huafon Group Co., Ltd. | PUR-Ester | Huafon |
| ISPLEN® RC 580 S2M | REPSOL | PP, Unspecified | ISPLEN® |
| MAJORIS GFR320 | AD majoris | PP, Unspecified | MAJORIS |