RTP 199 X 127145 F

Category: PP, Unspecified , Polypropylene
Manufacturer: RTP Company
Trademark: RTP
Fillers: -
Ports: Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms FOB, CIF, DAP, DAT, DDP
PDF: 0HIYXt_RTP-199-X-127145-F.pdf
PRICE: ​Order Products​ email   sales@su-jiao.com
Wechat: WECHAT
Message
Flame Retardant - Glass Fiber - Chemically Coupled - Non-PBB/PBDE
General Information
Filler / Reinforcement
  • Glass Fiber
Features
  • Chemically Coupled
  • Flame Retardant
RoHS Compliance
  • Contact Manufacturer
Processing Method
  • Injection Molding
PhysicalNominal ValueUnitTest Method
Specific Gravity 1.31g/cm³ASTM D792
Molding Shrinkage - Flow (3.20 mm)0.10 to 0.30%ASTM D955
MechanicalNominal ValueUnitTest Method
Tensile Modulus 6550MPaASTM D638
Tensile Strength 58.6MPaASTM D638
Tensile Elongation (Yield)2.0 to 5.0%ASTM D638
Flexural Modulus 6550MPaASTM D790
Flexural Strength 100MPaASTM D790
ImpactNominal ValueUnitTest Method
Notched Izod Impact (3.20 mm)120J/mASTM D256
Unnotched Izod Impact (3.20 mm)530J/mASTM D4812
ThermalNominal ValueUnitTest Method
Deflection Temperature Under Load (1.8 MPa, Unannealed)135°CASTM D648
FlammabilityNominal ValueTest Method
Flame Rating UL 94
    1.50 mm V-0
    3.00 mm 5VA
InjectionNominal ValueUnit
Drying Temperature 79.4°C
Drying Time 2.0hr
Processing (Melt) Temp 191 to 232°C
Mold Temperature 32.2 to 65.6°C
Injection Pressure 68.9 to 103MPa
Resin Grade Manufacturer Category Trademark
SEPTON™ 2004 Kuraray Co., Ltd. SEPS SEPTON™
StarGRIP GP 45-9000 STAR Thermoplastic Alloys & Rubbers, Inc. TPE StarGRIP
ABS Proquigel LS Proquigel ABS ABS Proquigel
Complet® LCF20-LGF20-PA66 PlastiComp, Inc. Nylon 66 Complet®
HiFill® PA6/6 GF13 L Techmer Engineered Solutions Nylon 66 HiFill®