LNP™ LUBRICOMP™ WFP36 compound
| Category: | PBT , Polybutylene Terephthalate |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ LUBRICOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 0GhbgL_LNPLUBRICOMPWFP36compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP LUBRICOMP* WFP36 is a compound based on Polybutylene Terephalate resin containing Silicone, Glass Fiber, PTFE. Added features of this material include: Internally Lubricated. Also known as: LNP* LUBRICOMP* Compound WFL-4536 Product reorder name: WFP36 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.58 | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage | |||
| Flow : 24 hours | 0.10 - 0.30 | % | ASTM D955 |
| Transverse flow : 24 hours | 0.50 - 1.0 | % | ASTM D955 |
| Vertical flow direction : 24 hours | 0.50 - 1.0 | % | ISO 294-4 |
| Flow direction : 24 hours | 0.10 - 0.30 | % | ISO 294-4 |
| Water Absorption (24 hr, 50% RH) | 0.40 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 10300 | MPa | ASTM D638 |
| -- | 11800 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Fracture | 113 | MPa | ASTM D638 |
| Fracture | 118 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Fracture | 2.5 | % | ASTM D638 |
| Fracture | 2.7 | % | ISO 527-2 |
| Flexural Modulus | |||
| -- | 8740 | MPa | ASTM D790 |
| -- | 9360 | MPa | ISO 178 |
| Flexural Strength | |||
| -- | 194 | MPa | ASTM D790 |
| -- | 189 | MPa | ISO 178 |
| Coefficient of Friction | ASTM D3702 Modified | ||
| With self-dynamics | 0.50 | ASTM D3702 Modified | |
| With Self-Static | 0.42 | ASTM D3702 Modified | |
| Wear Factor - Washer | 136 | 10^-10 in^5-min/ft-lb-hr | ASTM D3702 Modified |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 69 | J/m | ASTM D256 |
| 23°C 2 | 10 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 580 | J/m | ASTM D4812 |
| 23°C 3 | 47 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Energy at Peak Load | 7.51 | J | ASTM D3763 |
| -- | 14.1 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 1.8 MPa, unannealed, 3.20mm | 214 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 64.0mm span 4 | 213 | °C | ISO 75-2/Af |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.050 | % | |
| Rear Temperature | 221 - 232 | °C | |
| Middle Temperature | 243 - 254 | °C | |
| Front Temperature | 260 - 271 | °C | |
| Processing (Melt) Temp | 238 - 266 | °C | |
| Mold Temperature | 82.2 - 98.9 | °C | |
| Back Pressure | 0.172 - 0.344 | MPa | |
| Screw Speed | 30 - 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 |
| 4 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Staramide A28K | Eurostar Engineering Plastics | Nylon 66 | Staramide |
| BorPure™ MB7541 | Borealis AG | HDPE | BorPure™ |
| Americas Styrenics MC9540 | Americas Styrenics LLC | PS (GPPS) | Americas Styrenics |
| Fainplast PVC RKS 218/W | Fainplast Compounds S.r.l | PVC, Rigid | Fainplast PVC |
| Karina BLACK PVC COMPOUND 880-48/ 1-E-IS-LMP | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |