Plenco 00755 (Transfer)
| Category: | Mel Phenolic , Melamine Phenolic |
| Manufacturer: | Plastics Engineering Co. |
| Trademark: | Plenco |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 0GcR3F_Plenco-00755-Transfer-.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PLENCO 00755 is a melamine-phenolic copolymer molding compound offering excellent electrical and flame resistant properties. Type ASTM 5948 CMG, and UL recognized under component file E40654. 00755 is available only in brown. |
| General Information | |
|---|---|
| Features |
|
| UL File Number |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.60 | g/cm³ | ASTM D792 |
| Apparent Density | 0.58 | g/cm³ | ASTM D1895 |
| Molding Shrinkage - Flow | 0.68 | % | ASTM D955 |
| Water Absorption (24 hr) | 0.43 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (E-Scale) | 76 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 10800 | MPa | ASTM D638 |
| Tensile Strength | 56.0 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 0.70 | % | ASTM D638 |
| Flexural Modulus | 8510 | MPa | ASTM D790 |
| Flexural Strength | 84.6 | MPa | ASTM D790 |
| Compressive Strength | 166 | MPa | ASTM D695 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | 21.5 | J/m | ASTM D256 |
| Notched Izod Impact | 19 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 186 | °C | ASTM D648 |
| Continuous Use Temperature | 155 | °C | ASTM D794 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.5E+12 | ohms·cm | ASTM D257 |
| Dielectric Strength | ASTM D149 | ||
| -- 1 | 7.7 | kV/mm | ASTM D149 |
| -- 2 | 5.8 | kV/mm | ASTM D149 |
| Dielectric Constant (1 MHz) | 7.30 | ASTM D150 | |
| Dissipation Factor (1 MHz) | 0.073 | ASTM D150 | |
| Arc Resistance | 186 | sec | ASTM D495 |
| Comparative Tracking Index (CTI) | 500 | V | UL 746 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.50 mm) | V-0 | UL 94 |
| Additional Information |
|---|
| The value listed as Mold Shrink, Linear-Flow, ASTM D955 was tested according to the ASTM D6289 standard.The value listed as Comparative Tracking Index, UL 746 was tested according to ASTM D3638.Post Shrinkage, ASTM D6289, 240hr, 105°C: 0.96%Heat Resistance, ASTM D794: 155°CDrop Ball Impact, PLENCO Method: 101 J/m |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Mold Temperature | 150 - 177 | °C | |
| Back Pressure | 0.300 | MPa | |
| Screw Speed | < 60 | rpm |
| Injection instructions |
|---|
| Transfer Time: 3-8 secTransfer Pressure: 5.5-6.9 MPaPreheating temperature: 104-115°C |
| Note Message | |
|---|---|
| 1 . | Method A (short time) |
| 2 . | Method B (step by step) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 299 X 94743 E | RTP Company | Nylon 66 | RTP |
| TEPCON® M90 | Polyplastics Co., Ltd. | Acetal (POM) Copolymer | TEPCON® |
| EVALENE® PP PHF1001 | JG Summit Petrochemical Corporation | PP Homopolymer | EVALENE® PP |
| Gallonprene® GP520-7505 | Shenzhen Sungallon Rubber & Plastic Corporation Limited | TPE | Gallonprene® |
| OTECH ALLOY NT7000-70 - Profile | OTECH Corporation | TP, Unspecified | OTECH ALLOY |