Next Nylon 66 Prime Series PGHSLR33-01BK
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Next Polymers Ltd. |
| Trademark: | Next Nylon 66 Prime Series |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 0GKnwU_Next-Nylon-66-Prime-Series-PGHSLR33-01BK.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Description PA66 Glass Fiber Reinforced Heat stabilized Hydrolysis resistant Black compound Product Applications This grade is recommended for molded parts exposed to high temperatures and in contact with oils and greases, under the hood application such as radiator end tanks, Engine supports brake, clutch and gas pedals. Benefits Fatigue resistant, Fuel/oil/greases resistant, Anti freeze resistant & creep resistant with a good balance of strees- strain behavior. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Appearance |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Specific Gravity | 1.39 | -- | g/cm³ | ASTM D792 |
| Molding Shrinkage | ASTM D955 | |||
| Flow | 0.30 | -- | % | ASTM D955 |
| Transverse flow | 0.90 | -- | % | ASTM D955 |
| Water Absorption | ASTM D570 | |||
| 23°C, 24 hr | 1.2 | -- | % | ASTM D570 |
| Saturation 1 | 6.4 | -- | % | ASTM D570 |
| Hardness | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Rockwell Hardness | ASTM D785 | |||
| Class m | 110 | -- | ASTM D785 | |
| Class r | 125 | -- | ASTM D785 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Strength | 190 | 130 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 3.0 | 5.0 | % | ASTM D638 |
| Flexural Modulus | 10000 | 7200 | MPa | ASTM D790 |
| Flexural Strength | 260 | 210 | MPa | ASTM D790 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Notched Izod Impact (23°C) | 120 | 140 | J/m | ASTM D256 |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | |||
| 0.45 MPa, not annealed | 260 | -- | °C | ASTM D648 |
| 1.8 MPa, not annealed | 253 | -- | °C | ASTM D648 |
| Melting Temperature | 262 | -- | °C | ASTM D2117 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | 1.0E+14 | -- | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+15 | -- | ohms·cm | IEC 60093 |
| Dielectric Strength | 32 | -- | kV/mm | IEC 60243-1 |
| Comparative Tracking Index | 600 | -- | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating (0.800 mm) | HB | -- | UL 94 |
| Additional Information |
|---|
| 干燥 This grade is not suitable for food contact, medical devices or toy applications |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature - Hot Air Dryer | 80.0 | °C | |
| Drying Time | 4.0 - 6.0 | hr | |
| Suggested Max Moisture | 0.20 | % | |
| Rear Temperature | 260 - 270 | °C | |
| Middle Temperature | 270 - 280 | °C | |
| Front Temperature | 280 - 290 | °C | |
| Mold Temperature | 70.0 - 100 | °C |
| Note Message | |
|---|---|
| 1 . | Immersed |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SILVER® VUL105-W40K/SPTW-55P | Guangdong Silver Age Sci & Tech. Co., Ltd | PVC, Unspecified | SILVER® |
| Sindustris PP EI5003 | Sincerity Australia Pty Ltd. | PP, Unspecified | Sindustris PP |
| Styrolution PS 3600/3601 | INEOS Styrolution Group GmbH | PS (GPPS) | Styrolution PS |
| APEX® 90-A481R-80-NT | Teknor Apex Company | PVC, Flexible | APEX® |
| OTECH PVC PL1001-3 - Plenum Insulation | OTECH Corporation | PVC, Unspecified | OTECH PVC |