CALIBRE™ 2061-6
| Category: | PC , Polycarbonate Resin |
| Manufacturer: | Trinseo |
| Trademark: | CALIBRE™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 0G84Aq_CALIBRE-2061-6.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
CALIBRE™ 2061-6 resin is suitable for steam and ethylene oxide sterilization required by the health care industry. CALIBRE 2061-6 provides excellent heat resistance, impact strength, and processability. CALIBRE 2061-6 resin is compliant with ISO 10993 (Biological Evaluation of Medical Devices) and is suitable for use in approved medical applications. This product contains mold release and is currently available in black color. Main Characteristics:
Applications:
|
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Appearance |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.20 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (300°C/1.2 kg) | 6.0 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 0.50 to 0.70 | % | ASTM D955 |
| Water Absorption | ASTM D570 | ||
| 23°C, 24 hr | 0.15 | % | |
| Equilibrium, 23°C, 50% RH | 0.32 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness | ASTM D785 | ||
| M-Scale | 73 | ||
| R-Scale | 118 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1 | 2410 | MPa | ASTM D638 |
| Tensile Strength 2 | ASTM D638 | ||
| Yield | 62.1 | MPa | |
| Break | 68.3 | MPa | |
| Tensile Elongation 3 | ASTM D638 | ||
| Yield | 6.0 | % | |
| Break | 150 | % | |
| Flexural Modulus 4 | 2410 | MPa | ASTM D790 |
| Flexural Strength 5 | 96.5 | MPa | ASTM D790 |
| Taber Abrasion Resistance | 45 | % | ASTM D1044 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 850 | J/m | ASTM D256 |
| Unnotched Izod Impact (23°C) | No Break | ASTM D256 | |
| Instrumented Dart Impact (23°C, Total Energy) | 89.3 | J | ASTM D3763 |
| Tensile Impact Strength (23°C) | 567 | kJ/m² | ASTM D1822 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Annealed | 145 | °C | |
| 1.8 MPa, Unannealed | 129 | °C | |
| 1.8 MPa, Annealed | 142 | °C | |
| Vicat Softening Temperature | 156 | °C | ASTM D1525 6 |
| CLTE - Flow (-40 to 82°C) | 6.8E-5 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 2.0E+17 | ohms·cm | ASTM D257 |
| Dielectric Strength | 17 | kV/mm | ASTM D149 |
| Dielectric Constant | ASTM D150 | ||
| 60 Hz | 3.00 | ||
| 1 MHz | 3.00 | ||
| Dissipation Factor | ASTM D150 | ||
| 50 Hz | 1.0E-3 | ||
| 1 MHz | 2.0E-3 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 3.00 mm | HB | ||
| 0.750 mm | V-2 | ||
| 1.50 mm | V-2 | ||
| Oxygen Index 7 | 26 | % | ISO 4589-2 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 | °C | |
| Drying Time | 3.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Suggested Max Regrind | 25 | % | |
| Rear Temperature | 271 to 288 | °C | |
| Middle Temperature | 277 to 299 | °C | |
| Front Temperature | 299 to 327 | °C | |
| Nozzle Temperature | 299 to 327 | °C | |
| Processing (Melt) Temp | 299 to 327 | °C | |
| Mold Temperature | 76.7 to 110 | °C | |
| Screw Speed | 40 to 70 | rpm | |
| Clamp Tonnage | 2.8 to 6.9 | kN/cm² | |
| Screw L/D Ratio | 15.0:1.0 | ||
| Screw Compression Ratio | 1.5:1.0 to 3.0:1.0 |
| Note Message | |
|---|---|
| 1 . | 51 mm/min |
| 2 . | 51 mm/min |
| 3 . | 51 mm/min |
| 4 . | Method I (3 point load), 2.0 mm/min |
| 5 . | Method I (3 point load), 2.0 mm/min |
| 6 . | Rate A (50°C/h), Loading 2 (50 N) |
| 7 . | This rating not intended to reflect hazards presented by this or any other material under actual fire conditions. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Quadrant EPP PSU 1000 | Quadrant Engineering Plastic Products | PSU | Quadrant EPP |
| Unichem 93-732A | Colorite Polymers | PVC, Unspecified | Unichem |
| HiFill® PC GF20 | Techmer Engineered Solutions | PC | HiFill® |
| INNOPOL® PP CS 2-8000 | Inno-Comp Ltd. | PP Copolymer | INNOPOL® PP |
| OMIKRON GR 51 K NERO | TECNOPOL | PP Homopolymer | OMIKRON |