EcoVid 80TFH
| Category: | PLA , Polylactic Acid |
| Manufacturer: | Greener Polymers Inc. |
| Trademark: | EcoVid |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 0G4VIZ_EcoVid-80TFH.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
EcoVid-80TFH is a blend for thermoforming processes involving thin walled material with a High Heat resistance index. The material, rated for 178F/80°C and could be frozen to -32°C. Mould crystallization will increase the heat deflection from 80°C to 110°C+ depending on the application. Composition: Ingeo PLA content with bio-degradable and compostable HDT additives. Applications: EcoVid-80TFH is a Thermoforming blend suitable lids for hot coffee cups. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.27 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) | ASTM D1238 | ||
| 190°C/2.16 kg | 6.0 | g/10 min | ASTM D1238 |
| 210°C/2.16 kg | 6.0 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 0.30 - 0.50 | % | |
| Relative Viscosity | 2.5 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield) | 62.1 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 3.5 | % | ASTM D638 |
| Flexural Strength | 108 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 16 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Glass Transition Temperature | 55.0 - 60.0 | °C | ASTM D3418 |
| Vicat Softening Temperature | 130 | °C | ASTM D1525 |
| Melting Temperature | 130 - 180 | °C | ASTM D3418 |
| Peak Crystallization Temperature (DSC) | 155 - 170 | °C | ASTM D3418 |
| Heat Distortion | 80 - 110 | °C | ASTM E2092 |
| Optical | Nominal Value | ||
|---|---|---|---|
| Clarity | NIL |
| Additional Information |
|---|
| Vapour Barrier Transmission Rate (ASTM E380): 20.1636 (sd +/- 0.3537)Oxygen Permeability (ASTM E380): 53.481 (sd +/- 0.249) |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Hopper Temperature | 145 - 155 | °C | |
| Rear Temperature | 145 - 165 | °C | |
| Middle Temperature | 165 - 195 | °C | |
| Front Temperature | 165 - 195 | °C | |
| Nozzle Temperature | 165 - 180 | °C | |
| Back Pressure | 1.03 - 2.76 | MPa | |
| Screw Speed | 35 - 65 | rpm |
| Injection instructions |
|---|
| Mould Cycle Time: 19-35 secs |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SARAN™ XU 32019.40 Blend | The Dow Chemical Company | PVDC | SARAN™ |
| Titacon® CF910 | Titan Plastics Compounds Co., Ltd. | Acetal (POM) Copolymer | Titacon® |
| Geon™ Vinyl Flexible XV3855 | PolyOne Corporation | PVC, Flexible | Geon™ Vinyl Flexible |
| Edgetek™ PC-10GF/000 BLACK | PolyOne Corporation | PC | Edgetek™ |
| LNP™ LUBRICOMP™ RX06480 compound | SABIC Innovative Plastics | Nylon 66 | LNP™ LUBRICOMP™ |