Sumitomo Phenolic FM 1132P
| Category: | Phenolic , Phenolic |
| Manufacturer: | Sumitomo Bakelite North America, Inc. |
| Trademark: | Sumitomo Phenolic |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 0G3H1I_Sumitomo-Phenolic-FM-1132P.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| FM 1132P is a two-stage phenolic molding compound reinforced with cellulose in pellet form. FM-1132P is recommended to customers desiring approval under ASTM D-5948-96,Type CFI-10. (Replaces Military Specification MIL-M-14H.) |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Agency Ratings |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.37 | g/cm³ | ASTM D792 |
| Apparent Density | 0.40 | g/cm³ | ASTM D1895 |
| Molding Shrinkage - Flow (Compression Molded) | 0.30 | % | ASTM D955 |
| Water Absorption (24 hr) | 0.60 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (E-Scale, Compression Molded) | 115 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Compression Molded) | 45.0 | MPa | ASTM D638 |
| Flexural Modulus (Compression Molded) | 8000 | MPa | ASTM D790 |
| Flexural Strength (Compression Molded) | 70.0 | MPa | ASTM D790 |
| Compressive Strength | 193 | MPa | ASTM D695 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (Compression Molded) | 59 | J/m | ASTM D256A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, Compression Molded) | 180 | °C | ASTM D648 |
| RTI Elec | 150 | °C | UL 746 |
| RTI Imp | 150 | °C | UL 746 |
| RTI Str | 150 | °C | UL 746 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Dielectric Strength 1 | ASTM D149 | ||
| -- 2 | 7.2 | kV/mm | |
| -- 3 | 4.8 | kV/mm |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.60 mm) | HB | UL 94 |
| Note Message | |
|---|---|
| 1 . | Wet, 60 Hz |
| 2 . | Method A (Short-Time) |
| 3 . | Method B (Step-by-Step) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RJM SN501G30 | RJM International, Inc. | Nylon 6 | RJM |
| ACLAR® UltRx 3000 | Honeywell | PCTFE | ACLAR® |
| Akulon® Ultraflow K-FHG7 /A | DSM Engineering Plastics | Nylon 6 | Akulon® Ultraflow |
| EPT K-9720 | Mitsui Chemicals, Inc. | EPDM | EPT |
| Sylvin 7833-85 Yellow 4113 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |