Ultradur® B 4040 G4
| Category: | PBT+PET , Polybutylene Terephthalate + PET |
| Manufacturer: | BASF Corporation |
| Trademark: | Ultradur® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 0G3G3w_Ultradur-B-4040-G4.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Injection molding grade with 20 % glass fibers for industrial parts with excellent surface quality, for example external door handles in vehicles, visible sunroof frames, oven door handles, toaster casings, external mirrors, rear screen wiper arms in vehicles and sunroof wind deflectors. Formerly called KR 4040 G4. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Multi-Point Data |
|
| Resin ID (ISO 1043) |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.47 | g/cm³ | ISO 1183 |
| Apparent Density | 0.70 to 0.80 | g/cm³ | |
| Melt Volume-Flow Rate (MVR) (275°C/2.16 kg) | 22.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage | ISO 294-4 | ||
| Across Flow | 0.90 | % | |
| Flow | 0.40 | % | |
| Water Absorption | ISO 62 | ||
| Saturation, 23°C | 0.40 | % | |
| Equilibrium, 23°C, 50% RH | 0.20 | % | |
| Viscosity Number 1 | 105 | cm³/g | ISO 307 |
| Mold Shrinkage 2 | |||
| free, longitudinal | 0.21 | % | |
| free, transverse | 1.1 | % |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Maximum Service Temperature - short cycle operation | 210 | °C |
| Additional Information | Nominal Value | Test Method | |
|---|---|---|---|
| Automotive Materials (> 1.00 mm) | Passed | FMVSS 302 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Screw Speed | < 250 | mm/sec |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Ball Indentation Hardness (H 358/30) | 190 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 7500 | MPa | ISO 527-2 |
| Tensile Stress (Break) | 120 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 2.8 | % | ISO 527-2 |
| Flexural Modulus | 7010 | MPa | ISO 178 |
| Flexural Stress | 190 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 5.5 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -30°C | 40 | kJ/m² | |
| 23°C | 40 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 215 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 180 | °C | ISO 75-2/A |
| Melting Temperature | 223 | °C | ISO 11357-3 |
| CLTE - Flow (23 to 80°C) | 2.0E-5 to 3.0E-5 | cm/cm/°C | ISO 11359-2 |
| Specific Heat | 1100 | J/kg/°C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | > 1.0E+13 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+16 | ohms·cm | IEC 60093 |
| Relative Permittivity | IEC 60250 | ||
| 100 Hz | 3.70 | ||
| 1 MHz | 3.50 | ||
| Dissipation Factor | IEC 60250 | ||
| 100 Hz | 1.4E-3 | ||
| 1 MHz | 0.018 | ||
| Comparative Tracking Index (Solution A) | 300 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flammability Classification | IEC 60695-11-10, -20 | ||
| 0.800 mm | HB | ||
| 1.60 mm | HB |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 to 120 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.040 | % | |
| Hopper Temperature | 80.0 | °C | |
| Rear Temperature | 260 | °C | |
| Middle Temperature | 265 | °C | |
| Front Temperature | 270 | °C | |
| Nozzle Temperature | 270 | °C | |
| Processing (Melt) Temp | 250 to 280 | °C | |
| Mold Temperature | 60.0 to 100 | °C |
| Note Message | |
|---|---|
| 1 . | solution 0,005 g/ml Phenole/1,2 Dichlorbenzol 1:1 |
| 2 . | plate with film gate 150*150*3 mm³ |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 282 B TFE 15 | RTP Company | Nylon 610 | RTP |
| Radilon® S CV300 100 NAT | Radici Plastics | Nylon 6 | Radilon® |
| DJSilicone NE-5170 | DONGJUE SILICONE (NANJING) CO., LTD | Silicone | DJSilicone |
| Lion Idemitsu Composites PPS C-200SC | Lion Idemitsu Composites Co., Ltd. | PPS | Lion Idemitsu Composites PPS |
| Karina CRYSTAL PVC COMPOUND -E 75/320-IS-RG | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |