POCAN® BF 4232 HR 901510
| Category: | PBT , Polybutylene Terephthalate |
| Manufacturer: | LANXESS GmbH |
| Trademark: | POCAN® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 0FxLxz_POCANBF4232HR901510.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PBT, 30 % glass fibers, injection molding, flame retardant, hydrolysis stabilized |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Processing Method |
|
| Resin ID (ISO 1043) |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (23°C) | 1.67 | g/cm³ | ISO 1183 |
| Apparent Density | 0.70 | g/cm³ | ISO 60 |
| Melt Volume-Flow Rate (MVR) (260°C/2.16 kg) | 16.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage | ISO 294-4 | ||
| Vertical flow direction : 260°C, 2.00mm 1 | 1.1 | % | ISO 294-4 |
| Vertical flow direction : 120°C, 2 hours, 2.00mm 2 | 0.10 | % | ISO 294-4 |
| Flow direction : 260°C, 2.00mm 3 | 0.40 | % | ISO 294-4 |
| Flow direction : 120°C, 2 hours, 2.00mm 4 | 0.10 | % | ISO 294-4 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 9800 | MPa | ISO 527-2/1 |
| Tensile Stress (Break, 23°C) | 120 | MPa | ISO 527-2/5 |
| Tensile Strain (Break, 23°C) | 2.0 | % | ISO 527-2/5 |
| Flexural Modulus 5(23°C) | 10000 | MPa | ISO 178/A |
| Flexural Stress 6(23°C) | 185 | MPa | ISO 178 |
| Flexural Strain at Flexural Strength 7(23°C) | 2.3 | % |
| Additional Information | Nominal Value | Test Method | |
|---|---|---|---|
| ISO Shortname | PBT, GFHMRW, 09-100, GF30; ISO 1043-PBT GF FR (17) | ISO 7792 |
| Injection | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Residual Moisture Content | 0.0 - 0.020 | % | Karl Fisher |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | < 10 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 40 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact (23°C) | < 10 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength (23°C) | 35 | kJ/m² | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 215 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 195 | °C | ISO 75-2/A |
| Ball Pressure Test (212°C) | Pass | IEC 60695-10-2 | |
| Melting Temperature 8 | 225 | °C | ISO 11357-3 |
| Linear thermal expansion coefficient | ISO 11359-2 | ||
| Flow : 23 to 55°C | 3.0E-5 | cm/cm/°C | ISO 11359-2 |
| Lateral : 23 to 55°C | 1.0E-4 | cm/cm/°C | ISO 11359-2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Dielectric Strength (23°C, 1.00 mm) | 30 | kV/mm | IEC 60243-1 |
| Comparative Tracking Index (CTI) | PLC 3 | UL 746 | |
| Comparative Tracking Index (Solution A) | 225 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.400 mm | V-0 | UL 94 | |
| 0.800 mm | V-0 | UL 94 | |
| 1.50 mm | V-0 | UL 94 | |
| 3.00 mm | V-0 | UL 94 | |
| Glow Wire Flammability Index | IEC 60695-2-12 | ||
| 0.400 mm | 960 | °C | IEC 60695-2-12 |
| 0.800 mm | 960 | °C | IEC 60695-2-12 |
| 1.50 mm | 960 | °C | IEC 60695-2-12 |
| 3.00 mm | 960 | °C | IEC 60695-2-12 |
| Glow Wire Ignition Temperature | IEC 60695-2-13 | ||
| 0.400 mm | 900 | °C | IEC 60695-2-13 |
| 0.800 mm | 850 | °C | IEC 60695-2-13 |
| 1.50 mm | 725 | °C | IEC 60695-2-13 |
| 3.00 mm | 725 | °C | IEC 60695-2-13 |
| Oxygen Index 9 | 36 | % | ISO 4589-2 |
| Injection | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Drying Temperature - Circulation Dryer | 120 | °C | |
| Drying Time - Circulation Dryer | 4.0 - 8.0 | hr | |
| Processing (Melt) Temp | 240 - 260 | °C | |
| Mold Temperature | 80.0 - 100 | °C |
| Note Message | |
|---|---|
| 1 . | 60x60x2; MT 80°C; 600 Bar |
| 2 . | 60x60x2 |
| 3 . | 60x60x2; MT 80°C; 600 Bar |
| 4 . | 60x60x2 |
| 5 . | 2.0 mm/min |
| 6 . | 2.0 mm/min |
| 7 . | Pull Rate: 2 mm/min; 50% RH |
| 8 . | 10°C/min |
| 9 . | Procedure A |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| POLYTROPE® STR 3567EU-01 CLEAR | A. Schulman Inc. | Polyolefin, Enhanced (Capstock Resin) | POLYTROPE® |
| megol® P08 A60X3 | API SpA | SEBS | megol® |
| Moplen EP6036 | HMC Polymers | PP Impact Copolymer | Moplen |
| Trexprene® A88SCI-HF | Mitsubishi Chemical Performance Polymers, Inc. | TPV | Trexprene® |
| Chemlon® 66GF4H | Teknor Apex Company (Chem Polymer) | Nylon 66 | Chemlon® |