Starex GR-5035U
| Category: | SAN , Styrene Acrylonitrile |
| Manufacturer: | LOTTE ADVANCED MATERIALS CO., LTD. |
| Trademark: | Starex |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 0FaZ0Q_StarexGR5035U.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Starex GR-5035U is a styrene propylene fine (SAN) product, which contains glass fiber reinforced materials. It is available in North America, Africa and the Middle East, Latin America, Europe or Asia Pacific. Typical application areas are: architectural applications. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity (Natural) | 1.34 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (220°C/10.0 kg) | 6.0 | g/10 min | ASTM D1238, ISO 1133 |
| Molding Shrinkage | |||
| Flow : 3.20mm | 0.50 - 0.60 | % | ASTM D955 |
| Transverse flow : 3.20mm | 0.50 - 0.60 | % | ASTM D955 |
| Lateral flow : 3.20mm | 0.50 - 0.60 | % | ISO 2577 |
| Traffic : 3.20mm | 0.50 - 0.60 | % | ISO 2577 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness | |||
| Class r | 120 | ASTM D785 | |
| R scale | 123 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 9300 | MPa | ASTM D638 |
| -- | 9000 | MPa | ISO 527-2/50 |
| Tensile Strength | |||
| Yield 2 | 130 | MPa | ASTM D638 |
| Yield | 120 | MPa | ISO 527-2/50 |
| Fracture 3 | 120 | MPa | ASTM D638 |
| Fracture | 118 | MPa | ISO 527-2/50 |
| Tensile Elongation | |||
| Fracture 4 | 2.0 | % | ASTM D638 |
| Fracture | 2.0 | % | ISO 527-2/50 |
| Flexural Modulus | |||
| -- 5 | 9300 | MPa | ASTM D790 |
| -- 6 | 11500 | MPa | ISO 178 |
| Flexural Strength | |||
| -- 7 | 130 | MPa | ASTM D790 |
| -- 8 | 180 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 9(23°C) | 6.0 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact | |||
| 23°C, 3.18 mm | 59 | J/m | ASTM D256 |
| 23°C, 6.35 mm | 49 | J/m | ASTM D256 |
| 23°C 10 | 5.5 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, unannealed, 6.40mm | 109 | °C | ASTM D648 |
| 0.45 MPa, unannealed, 4.00mm | 110 | °C | ISO 75-2/B |
| 1.8 MPa, unannealed, 6.40mm | 105 | °C | ASTM D648 |
| 1.8 MPa, not annealed, 4.00mm | 106 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 113 | °C | ISO 306/B50 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Yellowness Index (2.50 mm) | 30 | YI | ASTM D1925 |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | 5.0 mm/min |
| 3 . | 5.0 mm/min |
| 4 . | 5.0 mm/min |
| 5 . | 2.8 mm/min |
| 6 . | 2.0 mm/min |
| 7 . | 2.8 mm/min |
| 8 . | 2.0 mm/min |
| 9 . | Thickness: 4mm |
| 10 . | Thickness: 4mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Makrolon® LQ3187 | Covestro - Polycarbonates | PC | Makrolon® |
| Shuman PP 510 | Shuman Plastics, Inc. | PP Homopolymer | Shuman PP |
| THERMOLAST® K TC4CSZ (Series: CS) | KRAIBURG TPE | TPE | THERMOLAST® K |
| Toyolac® 440Y MH5 | Toray Plastics (Malaysia) Sdn. Bhd. | ABS | Toyolac® |
| OmniPro™ HPP 10M FR0 | OMNI Plastics, LLC | PP Homopolymer | OmniPro™ |